磷酸改性天然石墨负极材料的设计、制备及性能研究

利用石墨层间化合物技术处理天然石墨,使磷酸进入到石墨层表面,并在石墨表面包覆一层有机胺中间体,然后在惰性气氛下进行高温处理。研究发现,所得材料在保持石墨原始结构不被破坏的情况下,增大了石墨的层间距,为锂离子的嵌入和脱出拓宽了通道,也为材料在充放电过程中预留了膨胀体积。将这种材料用于锂离子电池负极材料、电化学性能测试表明或改性材料中可具有更小的不可逆容量和更高的充放电效率,并且在大电流充放电情况下,倍率性能得到了提升。     

高性能复合石墨材料的研究

高性能复合石墨材料由石墨与合成树脂在一定温度和压力下模压复合而成。本文研究了各种石墨的配比、石墨的粒度、树脂的选用及复合工艺对复合材料物理、力学性能的影响,并对复合石墨材料断口进行了电镜分析。     

膨胀石墨的制备及结构研究

膨胀石墨具有耐高温、耐腐蚀、抗氧化、压缩性好等优点,在众多领域有着广泛的应用.作者研究了膨胀温度和膨胀时间对膨胀容积的影响,并用扫描电镜(SEM)对膨胀石墨的结构进行了分析.研究表明:温度在900 ℃,膨胀时间为30～50 s时,可膨胀石墨能发生良好的膨胀效果;膨胀石墨具有发达的孔隙结构,孔径尺寸在微米级,大小不一.     

膨胀石墨材料制备和除油的影响因素分析

针对水面浮油去除问题,研究了新型水面浮油去除材料———膨胀石墨(EG)的制备,分析了膨胀石墨的结构,通过实验研究了膨胀石墨对水上浮油的去除效果,研究了温度、pH值等因素对膨胀石墨浮油吸附效果的影响.结果表明:膨胀石墨材料对水面浮油处理效果受环境因素的影响较小,同传统的活性炭相比,吸附量大10~20倍.     

热压温度对Al2O3复合Bi0.5Sb1.5Te3材料热电性能的影响

为了制备高性能的热电材料,采用熔炼和机械粉碎制备成Bi0.5 Sb1.5 Te3粉末,再与α-Al2 O3纳米颗粒通过机械球磨混合,分别在50、100、150、200、230和260℃温度下保持332 M Pa压强下热压成型.XRD结果显示,随着热压温度的升高,样品衍射峰变窄、强度升高.从样品的SEM图片可以看出,热压...     

锂离子电池硅/石墨复合负极材料的制备及性能研究

锂离子电池发展的重要目标之一是高容量的负极材料,而硅材料以其高达4 200 mAh/g的理论比容量成为研究热点;但是硅负极材料有较大的体积效应,从而造成其电化学循环性能的快速下降,限制了其在生产中的应用.本研究以纳米硅与石墨不同比例的掺杂,通过高能球磨与退火处理,表明当硅与石墨比例为2：1时,首次放电比容量可达2 136.4 mAh/g,同时首次的充放电效率为85.5%; 经过35次循环之后,其可逆容量的保持率85.3%,具有良好的电化学性能.硅/石墨复合材料良好的电化学性能,使其在锂离子电池负极材料的生产及应用中具有重要研究价值.     

膨胀石墨/石蜡复合相变蓄热材料的制备及性能研究

以石蜡作为相变蓄热材料的基本材料,利用膨胀石墨的高吸附性和高导热性提高相变材料的传热性能,制备出不同配比的中低温相变蓄热材料,利用DSC测试出各组复合相变蓄热材料的热物性参数.研究结果表明:膨胀石墨含量不宜过多,应该小于5％;添加的膨胀石墨对石蜡相变点和焓变的影响很小.     

膨胀石墨/石蜡复合相变蓄热材料的制备及性能研究

以石蜡作为相变蓄热材料的基本材料,利用膨胀石墨的高吸附性和高导热性提高相变材料的传热性能,制备出不同配比的中低温相变蓄热材料,利用DSC测试出各组复合相变蓄热材料的热物性参数.研究结果表明:膨胀石墨含量不宜过多,应该小于5%;添加的膨胀石墨对石蜡相变点和焓变的影响很小.     

热压合成Ti2AlC材料及热力学分析

以Ti、Al元素粉和活性炭为原料，采用热压工艺合成了Ti2A1C块体材料。通过不同温度下合成试样的X-射线衍射分析（XRD），确定了热压合成试样的物相组成，并用扫描电子显微镜（SEM）观察了所合成试样的显微结构。结果表明：完全以元素粉为原料按2．0Ti／1．0Al／1．0C（摩尔比，下同）配比在1500℃热压60min能合成纯度高的Ti2AlC块体材料，产物中仅含有非常少的杂相TiC和Ti3AlC2。根据热力学计算结果，在Ti、Al和C三元系统中，TiC是最稳定的中间产物。另外，解释了在合成Ti2AlC过程中Ti3AlC2的产生。     

三元层状Ti_3AlC_2材料的制备及力学性能分析

分别以石墨和TiC为碳源,以微米级Ti粉、Al粉为原料,采用固-液相原位热压烧结方法制备了不同反应物合成的致密层状Ti3AlC2陶瓷材料.采用XRD、SEM分析了产物的形貌和相组成,并对其力学性能进行了分析测试.研究表明:在1 300℃、25 MPa条件下,以TiC/Al/Ti混合粉末体系为原料,热压烧结可以获得纯度较高的致密Ti3AlC2层状陶瓷材料;Ti3AlC2陶瓷材料的断裂韧度KIC为5.60 MPa.m1/2,维氏硬度在HV 400～600之间,抗弯强度为454.7 MPa,抗压强度可达764 MPa.研究表明,晶粒细化是其力学性能提高的主要原因.     

500MPa级钢筋混凝土结构的研究进展

在混凝土构件中使用500MPa级高强度钢筋可以明显地减少用钢量,显著提高工程质量,并能取得较好的社会经济效益.介绍了当前500MPa级钢筋混凝土结构的国内外研究现状,总结了国内500MPa级钢筋混凝土不同构件的试验,对500MPa级钢筋混凝土不同构件的主要试验研究成果作了阐述.同时对未来500MPa级钢筋混凝土结构的研究提出了建议.     

真空热压机加热供电系统改造

为改善企业产品规模不断扩大导致的旧式真空热压机无法满足压制要求的现状，并节约成本，对真空热压机供电系统进行了改造，并对改造方案的必要性和可行性及设备改造结果进行了验证．经实践证明，该改造方案很好地解决了生产需求和设备能力之间的矛盾，实现了以极低的投入换来较好的控制效果，节约了大量技术改造资金，提高了自动控制水平。大大减轻工作人员劳动强度，且提高了产品的合格率．     

Low-cost oriented preparation of ultra fine xonotlite fibers

Nanometer-sized xonotlite fibers have great potential application in many fields. The traditional method of preparing ultra fine xonotlite fibers uses the ultra fine and highly active silica as the major raw materials, which is not only expensive but also difficult to prepare the xonotlite fibers with diameters around 100 nm. In this study, the ultra fine xonotlite fibers with diameters around 100 nm were prepared by an autoclaving method. The preparation was low-cost oriented by using natural powder quartz and lime as the major raw materials. The intergrowth of the fibers formed thin shell hollow balls or ellipsoids, namely the secondary particles.The length of the nanometer-sized xonotlite fibers was around several microns. The fibers and their secondary particles were produced at 216℃ for 6 h with a continuous stirring of 300-500 r/min. Zirconium oxychloride was used as an additive. The experiments show that zirconium oxychloride has an enormous effect on the growing habit of xonotlite crystals and plays an important role in controlling the diameter of the xonotlite fibers.     

Multiple structure graphite stabilized stearic acid as composite phase change materials for thermal energy storageOA

This paper used 3 types of graphite with different physical structures as the porous matrix to prepare composite phase change materials(PCMs), and investigated their photo-thermal conversion performance and application in battery thermal management. Multiple structure graphite minerals, including microcrystalline graphite(MG), scale graphite(SG), and expanded graphite(EG) were used as porous matrix,while stearic acid(SA) acts as the phase change material. The vacuum impregnation method was appli...     

低硫柔性石墨的制备新工艺及微观结构分析

针对传统方法制得的膨胀石墨的硫含量高的问题,新工艺采用高锰酸钾和浓硫酸作复合氧化剂,三氯化铁作插入剂,制得的可膨胀石墨采用脱除硫酸、磷酸浸渍、脱磷酸、水洗至中性、低温干燥、1050℃高温膨化、压缩空气换气等工艺,使制得的柔性石墨的硫含量低于500μg/g．用扫描电子显微镜可观察到柔性石墨的层间距离明显增大．     

模压工艺对CF+G/PEEK复合材料力学性能的影响

采用模压法制备了碳短纤维和石墨混合填充聚醚醚酮复合材料,以拉伸强度和冲击韧性作为力学性能评价指标,探讨和分析了制备工艺对CF+G/PEEK复合材料力学性能的影响,优化出了较佳的模压制备工艺参数。实验结果表明,较佳的模压制备工艺参数为:为加热温度390℃、保温时间20min、保压温度320℃、保压压力43MPa、保压时间15min。     

各向同性石墨结构与工艺条件的关系

对比研究国外石墨IG-11、NBG-18和国产石墨HSM-SC的各向同性度、气孔直径、气孔形貌和微晶状态,探讨其结构差异.研究发现,国外石墨在各向同性度的控制上优于国产石墨;采用细颗粒配料方式下焦颗粒平均直径对石墨内部气孔直径的大小影响较大;在相同工艺条件下,采用细颗粒配料方式的石墨力学性能更好;细颗粒各向同性石墨质量与改进混捏均匀性有重要联系;利用X射线衍射谱中石墨(002)衍射峰的半高宽可以定性评价石墨化程度.探讨了国外各向同性石墨制备工艺中值得借鉴的地方.     

锂离子电池硅/石墨/碳负极材料性能

为提高锂离子电池硅基材料的循环性能,用高温固相热解法合成硅/石墨/碳复合材料.采用XRD、循环伏安和充放电技术表征其结构和电化学性能.考察不同的粘结剂体系和极片热处理对材料电化学循环性能的影响.结果表明:采用水性粘结剂可以提高材料的电化学性能;对极片进行热处理也可以很好地提高电极的循环稳定性.首次脱锂比容量为970.5 mAh/g,40次循环后,脱锂比容量仍高达822.1 mAh/g.     

沥青混合料生产中热料仓骨料颗粒组成的变异

从沥青混合料的目标和生产配合比出发，通过对沥青混合料生产过程中热料仓骨料落仓有所偏颇、骨料的取样筛分等过程进行跟踪分析，对可能发生的热料仓骨料颗粒组成的变异进行了探讨，旨在减少在实际生产中该变异的发生，使生产的沥青混合料的质量更趋稳定。     

硫化机的网络控制方案

为改进硫化机单机运行方式在大规模生产模式下存在的不足 ,设计了一种采用计算机和PLC网络对多台硫化机进行联网控制的新方案 ,集中地对联网的硫化机进行程序设定和实时监控 ,记录硫化过程数据 ,进行数据查询和管理 .该方案的应用能降低设备投资 ,提高轮胎质量 ,提升企业生产管理信息化水平 .