PLD方法制备的纳米Fe/Al薄膜的结构及应力分析

 采用PLD方法制备了Fe/Al合金薄膜，研究了Fe/Al合金薄膜的物相、结构、应力等。研究表明薄膜的沉积速率随着衬底温度的升高而降低。原子力显微镜（AFM）图像显示，薄膜表面平整、致密且光滑，均方根粗糙度小于1 nm。等离子体发射谱（ICP）表明Fe/Al原子比为1∶1。X射线小角衍射（XRD）分析表明薄膜中的物相是Al_0.5Fe_0.5，Al_0.5Fe_0.5晶体具有简单立方结构(SC)，晶格常数为0.297 nm，平均晶粒尺寸为81.74 nm，平均微畸变为0.007 6。     

采用空心阴极放电等离子体化学气相沉积方法制备a-CH薄膜

 研究了不同衬底-阴极距离、直流电压和H₂流量对a-CH薄膜沉积速率的影响。结果表明：衬底-阴极距离必须大于0.5cm，随着该距离的增加，薄膜的沉积速率减少；直流电压达550V时沉积速率最大；随着H2含量的增加，CH₄含量相对减少，沉积速率随之降低。用AFM观察了以该方法制得的448.4nm CH薄膜的表面形貌，表面粗糙度约为10nm。最后测出了不同条件下CH薄膜的UV-VIS谱，由此可以计算得到薄膜的禁带宽度及折射率。     

a-C∶H(N)薄膜结构的X射线光电子能谱分析

采用直流-射频等离子增强化学汽相沉积技术制备a-C∶H(N)薄膜，用X射线光电子能谱研究了混合气体中N₂含量对薄膜成分与结构的影响.a-C∶H(N)薄膜中含氮量可达9.09%.对a-C∶H(N)薄膜的C1s和N1s结合能谱的分析表明a-C∶H(N)薄膜的结构是由C₃N₄相镶嵌在sp²键结合的CN_x基体中组成.其中C₃N₄相中N和C原子比接近4∶3，不随薄     

YbF3沉积速率对红外激光薄膜表面缺陷的影响

 在介绍了薄膜缺陷的特点及成因的基础上，分析了YbF₃沉积速率对红外激光薄膜表面缺陷密度的影响，得出了镀制激光薄膜所需的合适速率。结果表明：薄膜表面缺陷主要以节瘤缺陷与陷穴缺陷为主，其缺陷密度随YbF₃沉积速率的减小基本表现为减小的趋势，当ZnS沉积速率约为0.2 nm/s，YbF₃沉积速率约为0.4 nm/s时，可得到比较满意的激光薄膜，薄膜表面缺陷密度仅为0.000 675。     

不同氮流量制备Mn3CuNx薄膜及其电、磁输运性质的研究

采用对靶磁控溅射方法在单晶Si(100)基片上制备了反钙钛矿结构的Mn₃CuN_x薄膜.通过控制制备过程中的反应气体氮气(N₂) 流量(N₂/Ar+N₂), 研究了氮含量对Mn₃CuN_x薄膜结构及物理性能的影响.分别利用X射线衍射仪、俄歇电子能谱、 原子力显微镜、X射线光电子能谱、物理性能测试系统和超导量子干涉仪, 对所制备薄膜的晶体结构、成分、表面形貌和电、磁输运性质进行了测试.结果表明:制备的薄膜均为反钙钛矿立方结构,且沿 (200) 晶面择优生长.随着氮含量的增大,薄膜表面粗糙度和颗粒度尺寸逐渐增大, 导致电阻率增加.氮含量对薄膜的电输运性质没有影响,所有薄膜电阻率均随着温度的降低逐渐增大, 呈现半导体型导电行为,这与对应的块体材料结果相反.Mn₃CuN_x薄膜随着测试温度的增大发生了 亚铁磁到顺磁的磁转变,且N含量的增大降低了磁有序转变温度,主要是由于N缺陷对Mn₆N八面体结构中 磁交换作用的影响所致.     

α-C:H膜表面形貌及光学性能的测试分析

 以H₂和反式-2-丁烯（T₂B）为工作气体，利用低压等离子体增强化学气相沉积法制备了α-C:H薄膜。采用原子力显微镜、扫描电镜测试了α-C:H薄膜的表面形貌，分析了实验参数对其形貌的影响。研究表明：固定压强(15 Pa)，当T₂B/H₂流量比为4时，薄膜均方根粗糙度可达0.97 nm。保持T2B/H2流量比固定，增加工作气压，薄膜均方根粗糙度减小，表面更平整、致密。利用傅里叶变换红外光谱仪对薄膜价键结构进行分析，结果表明：α-C:H薄膜中主要存在sp3C—H键，氢含量较高；T₂B/H₂流量比越低，薄膜中含有更多的C=C键。应用UV-VIS光谱仪，获得了波长在200～1 100 nm范围内薄膜的光吸收特性，α-C:H薄膜透过率可达98%，计算得到的折射率在1.16～1.40。随工作气压的增加，α-C:H薄膜中sp³杂化键增多，透过率、折射率增大。     

不同氧气流量对直流磁控溅射TiO2薄膜的影响

采用直流反应磁控溅射法,以高纯Ti为靶材,高纯O₂为反应气体,制备了TiO₂薄膜.研究了氧气流量对薄膜结晶取向、表面形貌和光学性能的影响.研究发现,TiO₂薄膜主要呈锐钛矿TiO₂(101)择优取向,当氧气流量较小时,薄膜中还含有金属Ti(100),氧气流量较大时,薄膜含TiO₂(101)和TiO₂(004),成多晶态;薄膜的粗糙度和颗粒大小都随氧气流量的增大而增大;薄膜在400~1100nm可见-近红外波段有较高的透射率并且其吸收峰随着氧气流量的增大而红移,当氧气流量为5sccm时,平均透射率最高.     

离子束辅助工艺中APS源偏转电压对HfO2薄膜性能的影响

 基于Leybold APS1104镀膜系统,采用离子束辅助反应沉积技术,以金属Hf粒为初始镀膜材料,APS源偏转电压为50~140 V范围内,在［100］单晶硅片和紫外石英（JGS1）基板上制备了HfO₂单层膜。分别利用Lambda 900分光光度计、X射线光电子能谱仪、X射线衍射仪以及原子力显微镜对HfO2薄膜的光谱性能、表面及纵向化学成分、晶相结构以及表面粗糙度进行了分析。结果表明：当APS源偏转电压在120~140 V及50~90 V两个范围内变化时,HfO2薄膜的紫外短波光学损耗随着偏转电压的降低而减小,而为110~90 V时紫外短波光学损耗对偏转电压的变化不敏感;偏转电压在50~140 V的范围内时,制备的HfO₂薄膜表面及纵向化学成分无明显变化;当偏转电压为100 V时,HfO₂薄膜晶粒尺寸及表面粗糙度分别达到最大值26.2 nm及5.79 nm,其后,随着偏转电压的降低,二者均逐渐减小。     

衬底温度对PLD制备的Mo薄膜结构及表面形貌的影响

 运用脉冲激光沉积(PLD)技术在Si(100)基片上沉积了金属Mo薄膜。在激光重复频率2 Hz,能量密度5.2 J/cm²,本底真空10^－6 Pa的条件下,研究Mo薄膜的结构和表面形貌,讨论了衬底温度对薄膜形貌与结构的影响。原子力显微镜(AFM)图像和X射线小角衍射(XRD)分析表明,薄膜表面平整、光滑,均方根粗糙度小于2 nm。沉积温度对Mo薄膜结构和表面形貌影响较大,在373~573 K范围内随着温度升高,薄膜粗糙度变小,结晶程度变好。     

直流三极溅射法制备CuInS2 薄膜

采用直流三极溅射装置制备获得了CuInS₂薄膜, 其中溅射靶采用一定面积比的[Cu]/[In]混合靶,反应气体采用CS₂气体. 本文中主要研究了0.02 Pa分压反应气体条件下不同面积比的[Cu]/[In]混合靶和沉积基板温度对CuInS₂薄膜结构和成分的影响, 其中CuInS₂薄膜制备所用时间为2 h生长的厚度为1—2 μm. 通过对CuInS₂薄膜的EPMA, X射线衍射测试分析表明, 最佳的CuInS₂薄膜可在面积比[Cu]/[In]混合靶为1.4:1和可控温度(150, 250和350 ℃)的条件下制备获得, 并且其结构被确认为黄铜矿结构. 通过实验结果计算出CuInS₂薄膜层有约为8.9%的C杂质含量.     

Microstructure and surface morphology of YSZ thin films deposited by e-beam technique

In present study yttrium-stabilized zirconia (YSZ) thin films were deposited on optical quartz (amorphous SiO₂), porous Ni-YSZ and crystalline Alloy 600 (Fe-Ni-Cr) substrates using e-beam deposition technique and controlling technological parameters: substrate temperature and electron gun power which influence thin-film deposition mechanism. X-ray diffraction, scanning electron microscopy (SEM), and atomic force microscopy (AFM) were used to investigate how thin-film structure and surface morphology depend on these parameters. It was found that the crystallite size, roughness and growth mechanism of YSZ thin films are influenced by electron gun power. To clarify the experimental results, YSZ thin-film formation as well evolution of surface roughness at its initial growing stages were analyzed. The evolution of surface roughness could be explained by the processes of surface mobility of adatoms and coalescence of islands. The analysis of these experimental results explain that surface roughness dependence on substrate temperature and electron gun power non-monotonous which could result from diffusivity of adatoms and the amount of atomic clusters in the gas stream of evaporated material.     

用锌有机源和CO2/H2混合气源PECVD沉积ZnO薄膜

在等离子体作用下,以CO2/H2混合气为氧源,Zn(C2H5)2锌为锌源,在单晶硅上生长出高度择优取向的氧化锌薄膜。X射线衍射分析表明,薄膜为六方结构,c轴高度择优;原子力显微镜观察到晶粒是有规律地按六方排布,薄膜的表面粗糙度较小;从光致发光谱还发现在380 nm处有非常强的紫外峰。     

Nanomechanical characterization of amorphous hydrogenated carbon thin films

Amorphous hydrogenated carbon (a-C:H) thin films deposited on a silicon substrate under various mixtures of methane-hydrogen gas by electron cyclotron resonance microwave plasma chemical vapor deposition (ECR-MPCVD) was investigated. Microstructure, surface morphology and mechanical characterizations of the a-C:H films were analyzed using Raman spectroscopy, atomic force microscopy (AFM) and nanoindentation technique, respectively. The results indicated there was an increase of the hydrogen content, the ratio of the D-peak to the G-peak (I_D/I_G) increased but the surface roughness of the films was reduced. Both hardness and Young's modulus increased as the hydrogen content was increased. In addition, the contact stress-strain analysis is reported. The results confirmed that the mechanical properties of the amorphous hydrogenated carbon thin films improved using a higher H₂ content in the source gas.     

The characterization of fluorocarbon films on NiTi alloy by magnetron sputtering

Fluorocarbon films were deposited on nickel-titanium (NiTi) alloy substrate by radio-frequency (RF, 13.56 MHz) magnetron sputtering using a polytetrafluoroethylene (PTFE) target. The deposition parameters of fluorocarbon films including the RF power, the working gas pressure and Ar flow rate were systematically studied. The structure of the deposited films was studied by attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) and X-ray photoelectron spectroscopy (XPS). The surface morphology of the deposited films was measured by atomic force microscopy (AFM). The mechanical properties of the deposited films were characterized by a nanoindenter. C-Fx and C-C units were found in the deposited fluorocarbon films, which corresponded to the results of XPS. The surface roughness of the fluorocarbon film was 7.418 nm (Ra).     

沉积工艺对二氧化锆薄膜生长特性影响的研究

利用反应离子束溅射、反应磁控溅射和电子束蒸发在K9基底上沉积ZrO2薄膜，并用原子力显微镜对薄膜表面形貌进行测量。通过数值相关运算，对不同工艺条件下薄膜生长界面进行定量描述，得到了薄膜表面的粗糙度指数、横向相关长度、标准偏差粗糙度等参量。由于沉积条件的不同，薄膜生长具有不同的动力学过程。在反应离子束溅射和反应磁控溅射沉积薄膜过程中，薄膜生长动力学行为均可用Kuramoto-Sivashinsky方程来描述，电子束蒸发制备薄膜的过程可以用Mullins扩散模型来描述，并发现在沉积薄膜过程中基底温度和沉积过程的稳定性对薄膜表面特征影响很大。     

Structural and tribological properties of cluster-assembled CNx films

We report the structural and tribological characterization of nanostructured CN_x thin films produced by the deposition of a supersonic carbon cluster beam assisted by nitrogen ion bombardment. The influence of the deposition parameters on the chemical composition and structure of the films has been systematically studied by X-ray photoelectron spectroscopy, elastic recoil detection analysis, transmission electron microscopy and atomic force microscopy. Depending on the deposition parameters, the films show a structure ranging from amorphous to disordered graphitic with interlinked planes. Nitrogen content depends on the nitrogen ion kinetic energy. The films have a very low density with a high surface roughness. Friction measurements at the nanoscale show a correlation between nitrogen content and mechanical properties of the system. PACS 61.46-w     

The effect of nitrogen pressure on the two-step method deposition of GaN films

GaN thin films were deposited on sapphire (0001) substrates at different nitrogen pressures by pulsed laser deposition (PLD) of GaN target in nitrogen atmosphere. Good single crystal GaN thin films were obtained after annealing at 1000 °C for 15 min in a NH₃ atmosphere. An Nd:YAG pulsed laser with a wavelength of 1064 nm was used as the laser source. The influence of nitrogen pressure on the thickness, crystallinity and surface morphology of GaN films were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM) and Raman spectroscopy. The results show that at low nitrogen pressure, the surface diffusion of adatoms can be influenced by the collisions between the nitrogen gas molecules and the activated atoms, which can influence the kinetic energy of the activated atoms. However, at high nitrogen pressure, the kinetic energy of adatoms is decided by the annealing temperature. In our experimental conditions, the GaN thin films deposited at 0.75 and 7.5 Pa have a high surface morphology and crystalline quality. PACS 71.55.Eq; 74.62.Fj     

含氮氟化类金刚石(FN-DLC)薄膜的研究：(Ⅲ)疏水性能分析

不同沉积条件下，在单晶硅基底上沉积了含氮氟化类金刚石(FN-DLC)薄膜，用静滴接触角/表面张力测量仪测量了水与FN-DLC膜表面的接触角.用X射线光电子能谱、Raman光谱和傅里叶变换吸收红外光谱(FTIR)分析了薄膜的组分和结构.用原子力显微镜观测了薄膜的表面形貌.结果表明，FN-DLC薄膜疏水性能主要取决于薄膜表面的化学结构、薄膜表面极化强度的强弱、以及薄膜的表面粗糙度的大小.sp³/sp²的比值减小，CF₂基团含量增加，薄膜粗糙度增加，接触角增大；反之，则接触角减小.在工艺上，沉积温度和功率的减小，气体流量比r(r=CF4/［CF₄+CH₄］)的增加，都会使水的浸润性变差，接触角增大. 关键词： 氟化类金刚石膜 疏水性 接触角     

Fe/Al混合膜的PLD法制备及表面分析

 采用脉冲激光气相沉积（PLD）技术制备了Fe/Al混合膜,测量了该混合膜的光电子能谱（XPS）,并采用原子力显微镜（AFM）、扫描电子显微镜（SEM）对Fe/Al混合膜作了表面分析。结果表明：Fe/Al混合膜的表面粗糙度对衬底温度有明显的依赖性, 随着衬底温度的升高,薄膜的表面逐渐变得平滑,膜层变得致密,在200 ℃衬底温度下制得了均方根（rms）粗糙度为0.154 nm、具有原子尺度光滑性的Fe/Al混合膜, 膜中Fe和Al分布比较均匀,其成分比约为1∶3,同时XPS分析也表明Fe/Al混合膜暴露在空气中后表面形成了Al₂O₃和FeO氧化层。     

氮气氛下(100)织构金刚石薄膜的成核与生长研究

利用热丝化学气相沉积法研究了氮气浓度对金刚石薄膜成核和生长的影响.实验发现氮气的 加入对金刚石成核密度影响不大,但促进了已形成的金刚石核的长大.适量的氮气不仅使金 刚石生长速率得到很大的提高,而且稳定了金刚石薄膜(100)面的生长,使金刚石薄膜具有 更好的(100)织构.利用原位光发射谱对衬底附近的化学基团进行了研究.研究表明,氮气的 引入使得金刚石生长的气相化学和表面化学性质发生了很大变化.含氮基团的萃取作用提高 了金刚石表面氢原子的脱附速率,从而提高了金刚石膜的生长速率.而含氮基团的选择吸附 使金刚石 关键词： 氮气 金刚石薄膜 织构 原位光发射谱