Porous Texture and Surface Character of Dehydroxylated and Rehydroxylated MCM-41 Mesoporous Silicas-Analysis of Adsorption Isotherms of Nitrogen Gas and Water Vapor

Four samples of MCM-41 mesoporous silicas whose average pore diameters are 2.4, 2.8, 3.2, and 3.6 nm were prepared using sodium orthosilicate and cationic surfactants of [CH(3)(CH(2))(n)N(CH(3))(3)]X (n=11, 13, 15, 17). These four samples were calcined at 1123 K in vacuo to obtain the dehydroxylated samples, which were further rehydroxylated at 298 K to obtain the rehydroxylated samples. The adsorption isotherms of nitrogen gas (77 K) for the 12 MCM-41 mesoporous silicas are of Type IVc, giving no adsorption hysteresis. On the other hand, the first adsorption isotherms of water vapor (298 K) for the dehydroxylated MCM-41 samples are quite different from those of nitrogen gas, giving the remarkable adsorption hysteresis. The second water isotherms for the rehydroxylated MCM-41 samples are of Type IV, showing slight hysteresis. Using the nitrogen isotherms, the relation between the pore size and carbon chain length of the surfactant has been determined, and the effect of dehydroxylation and rehydroxylation on the porous texture has been examined. Using the first and second water isotherms, the adsorption model of physisorbed waters adsorbed on the surface silanol groups has been proposed. From the pore size distribution curves of nitrogen and water, the presence of constrictions in the cylindrical pores has been predicted. Copyright 2000 Academic Press.     

Capillary condensation in mesoporous silica with surface roughness

We construct an atomistic silica pore model mimicking templated mesoporous silica MCM-41, which has molecular-level surface roughness, with the aid of the electron density profile (EDP) of MCM-41 obtained from X-ray diffraction data. Then, we present the GCMC simulations of argon adsorption on our atomistic silica pore models for two different MCM-41 samples at 75, 80, and 87 K, and the results are compared with the experimental adsorption data. We demonstrate that accurate molecular modeling of the pore structure of MCM-41 by using the experimental EDP allows the prediction of experimental capillary evaporation pressures at all investigated temperatures. The experimental desorption branches of the two MCM-41 samples are in good agreement with equilibrium vapor–liquid transition pressures from the simulations, which suggests that the experimental desorption branch for the open-ended cylindrical pores is in thermodynamic equilibrium.     

A density functional theory for Lennard-Jones fluids in cylindrical pores and its applications to adsorption of nitrogen on MCM-41 materials

A density functional theory (DFT) constructed from the modified fundamental-measure theory and the modified Benedict-Webb-Rubin equation of state is presented. The Helmholtz free energy functional due to attractive interaction is expressed as a functional of attractive weighted-density in which the weight function is a mean-field-like type. An obvious advantage of the present theory is that it reproduces accurate bulk properties such as chemical potential, bulk pressure, vapor-liquid interfacial tension, and so forth when compared with molecular simulations and experiments with the same set of molecular parameters. Capabilities of the present DFT are demonstrated by its applicability to adsorption of argon and nitrogen on, respectively, a model cylindrical pore and mesoporous MCM-41 materials. Comparison of the theoretical results of argon in the model cylindrical pore with those from the newly published molecular simulations indicates that the present DFT predicts accurate average densities in the pore, slightly overestimates the pore pressure, and correctly describes the effect of the fluid-pore wall interaction on average densities and pressures in the pore. Application to adsorption of nitrogen on MCM-41 at 77.4 K shows that the present DFT predicts density profiles and adsorption isotherms in good agreement with those from molecular simulations and experiments. In contrast, the hysteresis loop of adsorption calculated from the mean-field theory shifts toward the low pressure region because a low bulk saturated pressure is produced from the mean-field equation of state. The present DFT offers a good way to describe the adsorption isotherms of porous materials as a function of temperature and pressure.     

A grand canonical Monte Carlo study of capillary condensation in mesoporous media: effect of the pore morphology and topology

We study by means of Grand Canonical Monte Carlo simulations the condensation and evaporation of argon at 77 K in nanoporous silica media of different morphology or topology. For each porous material, our results are compared with data obtained for regular cylindrical pores. We show that both the filling and emptying mechanisms are significantly affected by the presence of a constriction. The simulation data for a constricted pore closed at one end reproduces the asymmetrical shape of the hysteresis loop that is observed for many real disordered porous materials. The adsorption process is a quasicontinuous mechanism that corresponds to the filling of the different parts of the porous material, cavity, and constriction. In contrast, the desorption branch for this pore closed at one end is brutal because the evaporation of Ar atoms confined in the largest cavity is triggered by the evaporation of the fluid confined in the constriction (which isolates the cavity from the gas reservoir). This evaporation process conforms to the classical picture of "pore blocking effect" proposed by Everett many years ago. We also simulate Ar adsorption in a disordered porous medium, which mimics a Vycor mesoporous silica glass. The adsorption isotherm for this disordered porous material having both topological and morphological defects presents the same features as that for the constricted pore (quasicontinuous adsorption and steep desorption process). However, the larger degree of disorder of the Vycor surface enhances these main characteristics. Finally, we show that the effect of the disorder, topological and/or morphological, leads to a significant lowering of the capillary condensation pressure compared to that for regular cylindrical nanopores. Also, our results suggest that confined fluids isolated from the bulk reservoir evaporate at a pressure driven by the smallest size of the pore.     

MCM-41分子筛的合成及129Xe核磁共振的研究

Purely siliceous MCM-41 with a narrow pore-size distribution, different pore size, high surface area was synthesized . As prepared, calcined and catalytically tested MCM-41 materials have been comprehensively characterized by N₂ adsorption/desorption at 77K and ¹²⁹Xe NMR. By adding mesitylene during the synthesis, the pore size of MCM-41 was enlarged to 5.2nm. The chemical shift in ¹²⁹Xe NMR spectroscopy of adsorbed xenon indicates that the MCM-41 is one dimensional pore channels .     

Nature of adsorption and desorption branches in cylindrical pores

To examine the nature of the adsorption and desorption branches in hysteretic adsorption isotherms of gases on mesoporous materials, we measured the temperature dependence of the adsorption and desorption isotherms of argon, oxygen, and carbon dioxide onto MCM-41 with a pore diameter of 4.4 nm. The results clearly show that in the open-ended cylindrical pores of MCM-41, capillary condensation rather than evaporation takes place near a thermodynamical equilibrium transition, as opposed to the general statement that capillary evaporation can occur via a meniscus formed at the pore mouth, and, thus, takes place at equilibrium.     

Density functional theory model of adsorption on amorphous and microporous silica materials

We present a novel quenched solid density functional theory (QSDFT) model of adsorption on heterogeneous surfaces and porous solids, which accounts for the effects of surface roughness and microporosity. Within QSDFT, solid atoms are considered as quenched component(s) of the solid-fluid system with given density distribution(s). Solid-fluid intermolecular interactions are split into hard-sphere repulsive and mean-field attractive parts. The former are treated with the multicomponent fundamental measure density functional. Capabilities of QSDFT are demonstrated by drawing on the example of adsorption on amorphous silica materials. We show that, using established intermolecular potentials and a realistic model for silica surfaces, QSDFT quantitatively describes adsorption/desorption isotherms of Ar and Kr on reference MCM-41, SBA-15, and LiChrosphere materials in a wide range of relative pressures. QSDFT offers a systematic approach to the practical problems of characterization of microporous, mesoporous, and amorphous silica materials, including an assessment of microporosity, surface roughness, and adsorption deformation. Predictions for the pore diameter and the extent of pore surface roughness in MCM-41 and SBA-15 materials are in very good agreement with recent X-ray diffraction studies.     

Hysteresis and scanning behavior of mesoporous molecular sieves

Sorption hysteresis is a widely studied phenomenon whose predicted behavior is well documented and researched. On the other hand, there is much less known about the region that lies between sorption isotherms, believed to be a metastable region. Scanning curves are a way of understanding the mechanism of hysteresis and a tool for hysteresis model validation. Scanning curves were produced for mesoporous materials: SBA-15 and MCM-41 for N(2) sorption at 77 K and Ar sorption at 87 K. A limited set of different scanning behaviors is identified. Like most hysteresis theories, it was found that a single model for scanning behavior cannot be extended to all materials under the same or different experimental conditions. Two behaviors are consistent with recent theories and simulations; however, several are not. The implications as to the characterization of pore dimensions and structure are discussed.     

有序介孔二氧化硅对正丁醛的吸附性能

合成了一系列具有不同孔结构与性质的有序介孔二氧化硅材料SBA-15、MCM-41、SBA-16、KIT-6, 同时通过改变水热温度制备了不同孔径大小的SBA-15, 并利用小角X射线散射、透射电镜、扫描电镜和氮气吸附-脱附等手段, 对其介孔结构进行了表征. 以正丁醛为探针分子, 考察了其对有机醛的吸附, 并与Y-沸石的吸附性能做了对比. 结果表明, 材料的介孔比表面积与其对正丁醛的吸附量成正比, 吸附等温线符合Langmuir 模型, 属于单层吸附, 具有最大介孔比表面积的MCM-41对正丁醛的吸附量最大(484 mg·g^-1). 最后将SBA-15添加到卷烟滤嘴中, 实验结果表明, SBA-15能显著降低卷烟烟气中巴豆醛的释放量.     

MCM-41分子筛和催化剂的特殊吸附等温线

测定了MCM-41中孔分子筛和催化剂的吸附等温线, 发现它们形状非常特殊, 不仅可逆部分分两段, 并且还存在两个滞后环, 在相对压力0.4以前出现的第一个滞后环可归属于中孔孔道内的毛细凝聚, 在饱和压力附近出现的第二个滞后环可归属于分子筛颗粒之间的毛细凝聚。利用吸附和XRD数据, 可有效地表征MCM-41分子筛和催化剂的结构有序度和孔道畅通情况。     

有序介孔二氧化硅对正丁醛的吸附性能

合成了一系列具有不同孔结构与性质的有序介孔二氧化硅材料SBA-15、MCM-41、SBA-16、KIT-6,同时通过改变水热温度制备了不同孔径大小的SBA-15,并利用小角X射线散射、透射电镜、扫描电镜和氮气吸附-脱附等手段,对其介孔结构进行了表征.以正丁醛为探针分子,考察了其对有机醛的吸附,并与Y-沸石的吸附性能做了对比.结果表明,材料的介孔比表面积与其对正丁醛的吸附量成正比,吸附等温线符合Langmuir模型,属于单层吸附,具有最大介孔比表面积的MCM-41对正丁醛的吸附量最大(484 mg·g-1).最后将SBA-15添加到卷烟滤嘴中,实验结果表明,SBA-15能显著降低卷烟烟气中巴豆醛的释放量.     

Atomistic model of micelle-templated mesoporous silicas: structural, morphological, and adsorption properties

The structural, morphological, and adsorption properties of MCM-41 porous silicas are investigated using a realistic numerical model obtained by means of ab initio calculations [Ugliengo, P.; et al. Adv. Mater.2008, 20, 1]. Simulated X-ray diffraction, small angle neutron scattering, and electronic microscopy for the atomistic model are in good agreement with experimental data. The morphological features are also assessed from chord length distributions and porous volume and specific geometrical surface calculations, etc. The N(2), CO(2), and H(2)O adsorption isotherms in the atomistic model of MCM-41 are also in reasonable agreement with their experimental counterpart. An important finding of the present work is that water forms a film adsorbed on specific hydrophilic regions of the surface while the rest of the surface is depleted in water molecules. This result suggests that the surface of MCM-41 materials is heterogeneous, as it is made up of both hydrophilic and hydrophobic patches. While adsorption and irreversible capillary condensation can be described using the thermodynamical approach by Derjaguin (also known as the Derjaguin-Broekhoff-De Boer model), the Freundlich equation fits nicely the data for reversible and continuous filling in small pores.     

Pseudocritical or hysteresis temperature versus pore size for simple fluids confined in cylindrical nanopores

The adsorption/desorption isotherms measured in nanoporous materials generally present a hysteresis. The hysteresis shrinks upon increasing the temperature (for a given pore size) or decreasing the pore size (for a given temperature), until it finally disappears at the so-called hysteresis (or pseudocritical) temperature T(h) or hysteresis (or pseudocritical) pore size R(h), not to be confused with a true critical point. In this paper, a Monte Carlo approach allowed calculating the surface free energy of confined fluid along the adsorption/desorption isotherms for various cylindrical pore sizes and temperatures. A simple phenomenological model then allowed exploiting these results to determine the relation between T(h) and R(h). The prediction is compared to various literature models and experimental data, showing agreement within uncertainties. On the other hand, the simulations cannot be used directly to predict T(h) and R(h) since they significantly overestimate the hysteresis width. The model predicts a nonlinear relation between the reduced hysteresis temperature and the inverse pore radius.     

Adsorption of crystal violet dye from aqueous solution using mesoporous materials synthesized at room temperature

In this work, batch adsorption experiments are carried out for crystal violet dye using mesoporous MCM-41 synthesized at room temperature and sulfate modified MCM-41 prepared by impregnation method using H₂SO₄ as sulfatising agent. The surface characteristics, pore structure, bonding behavior and thermal degradation of both the MCM-41 samples are characterized by nitrogen adsorption/desorption isotherms, X-ray diffraction (XRD) patterns, Fourier transform infrared (FT-IR) spectroscopy and thermo gravimetric analysis (TGA). The adsorption isotherm, kinetics and thermodynamic parameters are investigated for crystal violet (CV) dye using the calcined and sulfated MCM-41. Results are analysed using Langmuir, Freundlich and Redlich-Peterson isotherm models. It is found that the Freundlich model is an appropriate model to explain the adsorption isotherm. The highest adsorption capacity achieved is found to be 3.4×10⁻⁴ mol g⁻¹ for the sulfated MCM-41. The percentage removal of crystal violet dye increases with increase in the pH for both the MCM-41 adsorbents. Kinetics of adsorption is found to follow the second-order rate equation. From the thermodynamic investigation, it is evident that the adsorption is exothermic in nature.     

Diffusion of guest molecules in MCM-41 agglomerates

The pulsed field gradient nuclear magnetic resonance method has been used to study self-diffusion of cyclohexane in a commercial MCM-41 material at different external gas pressures from zero to saturated vapor pressure. It is found that the effective diffusivities exhibit three different regions with increasing pressure: decrease at low pressures, a sudden drop at intermediate pressures, and increase at higher pressures. In addition, in the region of irreversible adsorption (hysteresis loop) the diffusivities are also found to differ on the adsorption and the desorption branches. A simple analytical model taking account of different molecular ensembles with different transport properties due to the complex architecture of the porous structure is developed which provides a quantitative prediction of the experimental data. The analysis reveals that the effective diffusivity is predominantly controlled by the adsorption properties of the individual mesoporous MCM-41 crystallites which, in combination with high transport rates, provide a simple instrument for fine tuning of the transport properties by a subtle variation of the external conditions.     

Adsorption of toluene, methylcyclohexane and neopentane on silica MCM-41

Adsorption-desorption isotherms of toluene, methylcyclohexane and neopentane were determined on a silica MCM-41 material of pore diameter ∼3.4 nm over the temperature range 258 K to 308 K (278 K for neopentane). The isosteric enthalpies of adsorption were determined from the isotherms at the various temperatures. It was found that the isotherms of toluene and methylcyclohexane have a similar variation with the temperature, exhibiting hysteresis at 268 K and at lower temperature, while the adsorption of neopentane is reversible at all temperatures. The three organic adsorptives interact differently with the silica surface and the isosteric enthalpies of adsorption indicated that methylcyclohexane has the weakest interaction and toluene the strongest. A slight increase in the adsorption enthalpy at the beginning of the capillary condensation step is observed with methylcyclohexane and neopentane but not with toluene.     

Predicting neopentane isosteric enthalpy of adsorption at zero coverage in MCM-41

The isosteric enthalpy of adsorption for neopentane at relative pressures down to 3 × 10(-8) in MCM-41 was predicted for the temperature range from -15 to 0 °C. At such low pressures and temperatures, experimental measurements become problematic for this system. We used an atomistic model for MCM-41 obtained by means of a kinetic Monte Carlo method mimicking the synthesis of the material. The model was parametrized to represent experimental nitrogen adsorption isotherms at 77 K using grand canonical Monte Carlo simulations. The simulated isosteric enthalpy of adsorption shows very good agreement with available experimental data, demonstrating that GCMC simulations can predict heats of adsorption for conditions that are challenging for experimental measurements. Additional insights into the adsorption mechanisms, derived from energetic analysis at the molecular level, are also presented.     

Fluids in nanospaces: molecular simulation studies to find out key mechanisms for engineering

We have analyzed various phenomena that occur in nanopores, focusing on elucidating their key mechanisms, to advance the effective engineering use of nanoporous materials. As ideal experimental systems, molecular simulations can effectively provide information at the molecular level that leads to mechanistic insight. In this short review, several of our recent results are presented. The first topic is the critical point depression of Lennard-Jones fluid in silica slit pores due to finite size effects, studied by our original Monte Carlo (MC) technique. We demonstrate that the first layers of adsorbed molecules in contact with the pore walls act as a “fluid wall” and impose extra finite size effects on the fluid confined in the central portion of the pore. We next present a new kernel for pore size distribution (PSD) analysis, based entirely on molecular simulation, which consists of local isotherms for nitrogen adsorption in carbon slit pores at 77 K. The kernel is obtained by combining grand canonical Monte Carlo (GCMC) method and open pore cell MC method that was developed in the previous study. We show that overall trends of the PSDs of activated carbons calculated with our new kernel and with conventional kernel from non-local density functional theory are nearly the same; however, apparent difference can be seen between them. As the third topic, we apply a free energy analysis method with the aid of GCMC simulations to investigate the gating behavior observed in a porous coordination polymer, and propose a mechanism for the adsorption-induced structural transition based on both the theory of equilibrium and kinetics. Finally, we construct an atomistic silica pore model that mimics MCM-41, which has atomic-level surface roughness, and perform molecular simulations to understand the mechanism of capillary condensation with hysteresis. We calculate the work required for the gas–liquid transition from the simulation data, and show that the adsorption branch with hysteresis for MCM-41 arise from spontaneous capillary condensation from a metastable state.     

Nitrogen Adsorption Study of MCM-41 Molecular Sieves Synthesized Using Hydrothermal Restructuring

Nitrogen desorption scanning hysteresis loops (DSHLs) for large-pore MCM-41 silicas (pore diameter from 4.0 to 6.5 nm) are reported for the first time. DSHLs for MCM-41 were compared with those of conventional mesoporous silicas and no appreciable differences were found, although hysteresis loops and DSHLs for the latter were usually broader. Since desorption behavior of conventional porous silicas is appreciably influenced by pore connectivity, the observed similarity in hysteresis behavior suggests single-pore blocking effects for MCM-41 due to variation of pore diameter along its nonintersecting channels. It was also shown that the steepness of nitrogen desorption branches at relative pressures close to 0.4 often results from proximity of the lower pressure limit of adsorption-desorption irreversibility and consequently it is not justified to consider it as an indication of narrow pore size distribution. Thus, application of desorption data in calculations of pore size distributions may be grossly misleading.