制备方法对Mn-Ce/TiO2催化剂低温选择性催化还原活性的影响

采用溶胶凝胶法、浸渍法以及两者相结合的方法制备了Mn-Ce/TiO2催化剂。运用XRD、BET和SEM等技术对催化剂进行了表征,发现溶胶凝胶法制备的Mn-Ce/TiO2催化剂为锐钛矿结构,具有较大的比表面积,中孔结构丰富,Mn、Ce活性组分在载体表面高度分散或形成了无定形结构。实验研究了催化剂对氨选择性催化还原NO反应的催化性能,结果表明,用溶胶凝胶法制备的Mn-Ce/TiO2催化剂脱硝活性最好,当Mn、Ce负载量为20%,NH3/NO摩尔比为1.1,空速为9 436 h-1,烟气温度为240℃时,NO转化率大于90%。     

Ce掺杂改性对MnFe2O4低温选择性催化还原脱硝性能的影响研究

采用水热合成法制备了Ce掺杂MnFe2O4催化剂,用于低温选择性催化还原(SCR)脱硝.对催化剂晶型、脱硝性能和表面结构等进行分析,结果表明,Ce/(Fe+Mn)为0.5％(摩尔分数,下同)时催化剂表现出最优的SCR活性,80℃NO去除率可达100％;Ce/(Fe+Mn)分别为5.0％ 和10.0％ 时,催化剂80℃N...     

M_xO_y/碳纳米管的低温选择性催化还原脱硝性能研究

采用等体积浸渍法制备了MxOy(M表示V、Mn、Cu、Fe)/碳纳米管(CNTs)4种催化剂,用BET法、透射电子显微镜(TEM)和傅立叶红外光谱(FTIR)进行结构表征,并对其低温选择性催化还原(SCR)NO性能进行了考察和对比。结果表明,在NO为1248mg/m3、NH3为707mg/m3、O2为5%(体积分数)、气体总流量为700mL/min、反应温度为353～513K的条件下,不同催化剂存在不同的最佳活性温度,V2O5/CNTs催化剂在473K的较低温度下NO转化率达到最大,为82.9%;各催化剂活性均随着O2含量的增加先升高后降低,且变化幅度相似;在20～160min时,各催化剂活性随着反应时间的变化基本保持不变;催化剂活性均随氨氮比(NH3/NO)的增大先升高后降低,最佳NH3/NO为1.0(体积比)。     

Ce-Fe/ACF催化剂低温选择性催化还原NO的研究

以ACF作为载体制备了一系列不同质量分数的CeO2和Fe2O3混合负载型催化剂,研究了它们催化净化NO的低温活性和活性的稳定性。同时,对比研究了CeO2/ACF和Ce-Fe/ACF净化NO的能力。活性实验结果表明,催化剂中加入Fe2O3作为助催化,能使催化剂活性、稳定性等得到明显改善。反应温度为80~120℃时,比相同质量分数CeO2/ACF催化剂的NO脱除效率提高幅度最大达到18.11%,增幅度较大;随着反应温度的升高,催化剂的脱硝效率提高幅度趋小,反应温度为200℃时,两者相比,NO脱除效率仅提高1.98%;而后随着温度的攀升,催化剂的脱硝效率提高幅度又慢慢趋大,且其效率平稳。     

新型MnOx/CNTs催化剂低温选择性催化还原NO

采用等体积浸渍法制备了MnOx/CNTs催化剂,用于低温NH3选择性催化还原(SCR)NO的实验.使用BET,FT-IR,TEM和XRD对催化剂进行表征,结果表明:碳纳米管经混酸超声分散,增加了羧基活性基团,锰氧化物颗粒分布较均匀.在模拟烟气条件下,考察了催化剂的MnOx负载量、煅烧温度及质量和烟气流速比(W/F)对NO脱除率的影响.煅烧温度为773 K,MnOx负载量为10%时,NO脱除率达到98.56%;W/F为2～3 mg/(mL·min-1)时NO的脱除率更高.     

F掺杂改性及其制备方法优化对V2O5-WO3/TiO2催化剂低温SCR脱硝性能的影响

为提高SCR脱硝催化剂的低温脱硝性能,采用正交实验的方法制备了一系列氟（F）掺杂V2O5-WO3/TiO2催化剂,并对其进行活性分析,考察了不同氟元素来源（氟钛酸铵、氟化铵）、不同钒元素（V）前驱体（乙酰丙酮氧钒、偏钒酸铵）、钨元素（W）的不同添加方式（W做助剂、W既做载体又充当助剂）、不同载体制备方式（溶胶凝胶法、浸渍法）对催化剂脱硝性能的影响。结果表明,F掺杂改性显著增强了催化剂在200~350 ℃温度范围内的脱硝性能,其中以乙酰丙酮氧钒为V前驱体,以氟化铵为F源,W既充当载体又做助剂的方式制备出的F掺杂V2O5-WO3/TiO2催化剂具有最优的脱硝效果,其在空速为10 000 h-1的情况下,在200~350 ℃的温度反应区间,活性能稳定维持在98%以上。同时采用XPS、BET、TGA、SEM、XRD、Raman一系列表征手段对催化剂的理化性质进行了分析,表征结果表明F元素掺杂提高了活性组分在载体表面的分散度,同时促使了催化剂表面的电荷发生转移,增强了催化剂表面的氧化还原能力,促进了催化剂表面化学吸附氧的生成,增加了还原态V物种与还原态W物种的数量。     

CeO_x/AC催化剂NH_3选择性催化还原NO

以用不同浓度的HNO3预处理后的椰壳活性炭为载体,负载铈制备SCR催化剂。利用比表面积分析仪（BET）、X射线衍射（XRD）、扫描电镜（SEM）和催化剂活性实验,探讨了不同变量如金属离子的分布、焙烧温度和载体属性对催化活性的影响。结果表明,HNO3处理后,经500℃焙烧金属铈负载量为7%的催化剂表现出优良的催化性能。在90℃时,NO转化率在90%以上,随温度升高,达到接近100%的NO转化率。     

新型MnOx/CNTs催化剂低温选择性催化还原NO

采用等体积浸渍法制备了MnOx/CNTs催化剂,用于低温NH3选择性催化还原（SCR）NO的实验。使用BET,FT-IR,TEM和XRD对催化剂进行表征,结果表明：碳纳米管经混酸超声分散,增加了羧基活性基团,锰氧化物颗粒分布较均匀。在模拟烟气条件下,考察了催化剂的MnOx负载量、煅烧温度及质量和烟气流速比（W/F）对NO脱除率的影响。煅烧温度为773 K,MnOx负载量为10%时,NO脱除率达到98.56%;W/F为2-3 mg/（mL·min^-1）时NO的脱除率更高。     

CeOx/AC催化剂NH3选择性催化还原NO

以用不同浓度的HNO3预处理后的椰壳活性炭为载体,负载铈制备SCR催化剂。利用比表面积分析仪(BET)、X射线衍射(XRD)、扫描电镜(SEM)和催化剂活性实验,探讨了不同变量如金属离子的分布、焙烧温度和载体属性对催化活性的影响。结果表明,HNO3处理后,经500℃焙烧金属铈负载量为7%的催化剂表现出优良的催化性能。在90℃时,NO转化率在90%以上,随温度升高,达到接近100%的NO转化率。     

低温选择性催化还原脱除NOx的催化剂的研究进展

选择性催化还原(SCR)法是目前世界上应用较为成熟的烟气脱硝技术之一,由于传统的适用催化剂的起活温度偏高,因此开发低温高效、性能稳定的催化剂已成为该技术成功运用的关键.分析了SCR法的脱硝原理,对目前广泛研究的低温SCR催化剂的分类及其运用进行了综述,提出了研究中尚需解决的问题,最后展望了未来的研究方向.     

Effect of the Mn oxidation state and lattice oxygen in Mn-based TiO2 catalysts on the low-temperature selective catalytic reduction of NO by NH3

TiO₂-supported manganese oxide catalysts formed using different calcination temperatures were prepared by using the wet-impregnation method and were investigated for their activity in the low-temperature selective catalytic reduction (SCR) of NO by NH₃ with respect to the Mn valence and lattice oxygen behavior. The surface and bulk properties of these catalysts were examined using Brunauer-Emmett-Teller (BET) surface area, X-ray diffraction (XRD), temperature-programmed reduction (TPR), and temperature-programmed desorption (TPD). Catalysts prepared using lower calcination temperatures, which contained Mn⁴⁺, displayed high SCR activity at low temperatures and possessed several acid sites and active oxygen. The TPD analysis determined that the Brönsted and Lewis acid sites in the Mn/TiO₂ catalysts were important for the low-temperature SCR at 80～160 and 200～350 °C, respectively. In addition, the available lattice oxygen was important for attaining high NO to NO₂ oxidation at low temperatures.

Implications: Recently, various Mn catalysts have been evaluated as SCR catalysts. However, there have been no studies on the relationship of adsorption and desorption properties and behavior of lattice oxygen according to the valence state for manganese oxides (MnO_x). Therefore, in this study, the catalysts were prepared by the wet-impregnation method at different calcination temperatures in order to show the difference of manganese oxidation state. These catalysts were then characterized using various physicochemical techniques, including BET, XRD, TPR, and TPD, to understand the structure, oxidation state, redox properties, and adsorption and desorption properties of the Mn/TiO₂ catalysts.     

Fe-Mn基分子筛催化剂NH3低温选择性催化还原NO性能

采用柠檬酸法制备了不同Fe和Mn含量的Fe-Mn/HBeta催化剂,采用BET、XRD、SEM和XPS等方法对不同催化剂的特征参数进行表征,以氨气为还原剂,在空速为5 000 h-1的条件下,考察了活性成分负载量和焙烧温度对其活性的影响;探讨了催化剂的抗水抗硫性能.研究结果表明,焙烧温度为550℃、6%Fe-6%Mn/HBeta催化剂具有相对较优的催化活性,反应温度为90~230℃时,NO转化率为63.9%~96.99%,比表面积、孔体积和平均孔径分别为356.19 m2/g、0.61 cm3/g和16.83 nm,活性成分在催化剂表面高度分散,催化剂表面Mn主要以Mn3+和Mn4+存在,且以Mn4+居多;反应温度为180℃条件下,6%Fe-6%Mn/HBeta催化剂具有较好的抗水能力和同时抗水抗SO2能力,但单独抗SO2能力较差.     

六铝酸盐催化剂的催化还原脱硫脱硝性能

采用共沉淀法制备Cu和Fe掺杂的六铝酸盐催化剂(SrCuxFe1-xAl11O19-δ,x为0,0.2,0.4,0.5,0.6,0.8,1),通过XRD、TPR、BET等技术方法对催化剂的结构及性质进行了研究,并考察了以CO为还原剂的催化脱硝活性。结果表明,用碳酸铵作为沉淀剂在1 200℃焙烧4 h可以形成完整的六铝酸盐晶型,Cu和Fe能够取代Al3+,很好地促进六铝酸盐晶体结构的形成;SrCuxFe1-xAl11O19-δ催化剂有很好的脱硫脱硝催化活性,此类型的催化剂均使SO2、NO的转化率在空速为6 000 h-1下达到了80%和90%以上。向体系中加入氧气会对催化活性有较大影响。     

The effects of manganese precursors on Mn-based/TiO2 catalysts for catalytic reduction of NO with NH3

Manganese acetate (MnAc) and manganese nitrate (MnN) were employed as precursors for the preparation of MnAc)/TiO2, Mn (N)/TiO2, Mn(Ac)-Ce/TiO2, and Mn(N)-Ce/TiO2 by impregnation. These complexes were used as catalysts in the low-temperature selective catalytic reduction of NO with NH3. The influence of manganese precursors on catalyst characteristics, the reduction activity, and the stability of the catalysts to poisoning by H2O and SO2 were studied. Experiments showed that Mn(N) produced MnO2 with large grain sizes in Mn(N)/TiO2 catalyst. On the contrary, Mn(Ac) led to highly dispersed and amorphous Mn2O3 in Mn (Ac)/TiO2 catalyst, which had better catalytic activity and stability to SO2 at low temperatures. The doping of cerium reduced the differences in catalytic performance between the catalysts derived from different Mn precursors.     

Cu/Al-PILC催化的C3H6选择还原NO反应的研究

采用聚合羟基铝交联剂对蒙脱土进行撑柱,合成铝交联黏土(Al-PILC),并以其为载体,制备了应用于C3H6选择还原NO的催化剂Cu/Al-PLIC.考察了制备工艺条件及La2O3助剂对催化剂性能的影响,并采用DTA、IR技术对Al-PILC进行表征.研究结果表明,Al-PILC热稳定性随Al/clay比增加逐步提高,SO2-4改性Al-PILC上SO2-4与铝氧化柱形成了具有超强酸性的结构,催化活性得到显著提高;当Al/clay比为10 mmol/g,浸渍SO2-4量为20%(wt),Cu担载量为3%(wt),空速20 000 h-1时,Cu/Al-PILC在350℃NO转化率达到最大值52.02%;浸渍0.5%La2O3提高了Cu/Al-PILC催化剂的活性和热稳定性.