钨和钨合金真空固态压力扩散连接

以高纯铁粉为中间层,采用真空扩散连接实现纯W与W-60Fe合金材料的高强度连接,研究了连接工艺对元素扩散、连接性能和中间层组织、断口组织的影响.结果表明:连接界面发生梯度扩散并产生冶金结合,随扩散温度升高,W、Fe扩散距离呈抛物线性正增长;随扩散时间延长、施加压力增大,扩散距离都显著增大;且在W/Fe界面和(W-60F...     

17-4PH不锈钢和钛固态扩散连接的组织结构和性能

本文以钛和17-4沉淀硬化不锈钢为对象进行了固态扩散连接试验,试验条件为真空、单向压力3.5MPa,800~1050℃(50℃步幅)保温30min以及950℃保温30~180min(30min步幅)。采用光学显微镜,场发射扫描电子显微镜和X射线衍射技术对连接试样进行检测。直到850℃保温30min时,扩散界面上才形成Fe Ti相;然而,在保温30min时高于850℃以及950℃的任意保温时间内,会形成a-Fe+X、x、Fe2Ti和Fe Ti相及混合相。在950℃保温30min和以30?180min步幅的试验中,试样在1000℃时获得扩散连接最高的抗拉强度~326MPa,最高的剪切强度~254MPa及最高的冲击初性~24J。保温120min时获得的最高抗拉强度为?323MPa,最高剪切强度?243MPa及最高冲击韧性~221。连接件的残余应力随连接温度的升高及时间的延长而增大。     

Co-Cr-Mo合金和ZrO_2共烧结及其制品性能

为获得界面结合良好的Co-Cr-Mo合金/ZrO2连接,研究不同孔隙度的Co-Cr-Mo合金和ZrO2陶瓷分别在1 300、1 350、1 400℃下的单组元烧结行为以及Co-Cr-Mo合金与ZrO2的共烧结行为。测定烧结试样的密度与抗弯强度,利用扫描电镜(SEM)分析Co-Cr-Mo/ZrO2界面元素分布。结果表明:低孔隙度的Co-Cr-Mo合金收缩更快,因而可通过控制Co-Cr-Mo合金的孔隙度来控制其收缩,使其与ZrO2的收缩行为相近;随烧结温度升高,界面结合强度增加;相同温度下高孔隙度的Co-Cr-Mo与ZrO2的界面结合强度比低孔隙度的Co-Cr-Mo与ZrO2的界面结合强度大,1 400℃下烧结2 h,其界面结合强度达到35.06 MPa;随烧结温度升高和Co-Cr-Mo合金孔隙度增加,Co-Cr-Mo合金/ZrO2界面处的孔隙和裂纹减少,同时在垂直于界面方向存在1个1~2μm厚度的元素扩散区域。     

加热温度对镍中间层热轧钛钢复合板微观组织及力学性能的影响

以Ni为中间层制备钛/钢轧制复合板,借助扫描电镜、能谱仪、X射线衍射仪和Instron万能拉伸试验机等分析手段,研究了850～950℃加热温度对钛钢复合板力学性能和显微组织的影响。结果表明:当加热温度在850～900℃时,剪切强度随温度升高而升高;加热温度为900～950℃时,剪切强度随温度升高而降低,最高剪切强度都在900℃时获得。以Ni为中间层有效阻止了Fe和C等元素扩散到Ti侧形成金属间化合物,界面化合物种类不随温度变化,但化合物量随温度升高而增加。轧制温度为850℃时,界面上金属间化合物非常少,对应的剪切强度最低;轧制温度为900℃时,复合板界面剪切强度最优,与之相对应的界面结构是较为充分的元素扩散以及少量的金属间化合物;轧制温度为950℃时,金属间化合物层急剧变厚,TiNi_3和孔洞急剧增多,因而严重削弱了界面的剪切强度。     

Mn含量对Cu-Mn合金结构与性能的影响

基于Cu-Mn中间层可改善Cu与CuCrZr合金的连接性能,采用高能球磨法制备Cu-Mn合金粉末,研究烧结温度为650~850℃、Mn含量(质量分数)为10%~50%的Cu-Mn合金的烧结性能。结果表明:随Mn含量增加,Cu-Mn合金的相对密度和抗拉强度先增大后减小,但Mn含量过高时生成较多的Mn O,导致合金性能下降;随烧结温度升高,合金的相对密度和抗拉强度增大。850℃下烧结的67Cu-33Mn合金孔隙较小、组织均匀,其相对密度和抗拉强度均达到最大值,分别为91.62%和610.91 MPa,表明67Cu-33Mn合金具有最佳的烧结活性,宜作为Cu与CuCrZr合金连接的中间层。     

C/C与C/C-SiC复合材料连接件的高温热处理及微观结构

以硼改性酚醛树脂作为连接剂的主要成分,添加微米B_4C粉、纳米SiO_2粉和微米Mo粉作为填料,采用反应成形连接法连接C/C复合材料和C/C-Si C复合材料,并将连接件在300~1 400℃真空环境中热处理30 min。在室温环境下测量连接件的连接强度,计算不同温度下热处理后的强度保留率,并观察与分析连接层以及经连接强度测试后的断口形貌和元素分布。结果表明,连接件在1 200℃下热处理后,连接强度保留率取得极大值97.8%,连接层结构致密,孔洞、裂纹等缺陷较少;母材与胶层的界面处发生了C,O,Si,B和Mo元素的扩散;胶层中生成熔点及硬度都很高的Mo B和Si C,Mo B作为增强体与硼改性酚醛树脂裂解生成的玻璃碳形成复相陶瓷,从而提高连接件的强度保留率。     

基于W-Fe-Cr混合粉末中间层的钨/钢连接研究

以质量百分数组成为90W-8.5Fe-1.5Cr的W-Fe-Cr混合粉末为中间层,纯铜箔为钎料,采用1 120℃保温60 min并加压5 MPa的工艺参数,对纯钨和0Cr13Al钢进行真空连接。利用激光粒度分析仪、SEM、EDS和电子万能试验机等手段研究了W-Fe-Cr混合粉末形态、粒度分布以及接头的微观组织、成分、机械性能、剪切断口特征。结果表明,接头由钨母材/W-Fe-Cr高密度合金层/钢母材三部分组成,其中W-Fe-Cr高密度合金层由W-Fe-Cr混合粉末中间层固相烧结形成;W-Fe-Cr高密度合金层/钨母材界面通过极薄的钎缝实现钎焊连接;W-Fe-Cr高密度合金层/钢母材界面则通过先钎焊再固相扩散焊的机制连接。高能球磨制备W-Fe-Cr混合粉末对较小连接压力下生成均匀化、致密化的W-Fe-Cr高密度合金层具有关键作用。钨/钢接头剪切强度为41 MPa,断裂发生在W-Fe-Cr高密度合金层/钨母材结合界面,断面呈现为脆性断裂特征。本研究为线膨胀系数可调且不含活性元素Ni的钨/钢连接中间层设计提供了新思路,为进一步提高钨/钢连接结构在核聚变堆中的适用性进行了有益探索。     

镍基双合金扩散偶的拉伸性能研究

采用热等静压(HIP)扩散连接工艺,获得了镍基单晶高温合金与粉末高温合金的扩散偶。研究了热等静压和热处理工艺对扩散偶的组织和拉伸性能的影响。结果表明,不同温度热等静压的扩散偶均实现了冶金结合,瞬时拉伸断口位置处于DD402侧,断裂面为{111}滑移面。随着HIP温度升高,DD402母材的γ′相粒子粗化,FGH95粉末合金母材的再结晶晶粒长大;1 166℃HIP扩散偶热处理后,FGH95粉末合金的γ′相由晶界大尺寸γ′相、晶粒内中等尺寸的和细小的γ′相组成。扩散偶试样的650℃抗拉强度受HIP温度影响小,而屈服强度随着HIP温度升高而降低。     

W-Cu复合材料与Cu的扩散连接工艺

钨、铜热膨胀系数的过度失配,使得钨、铜的连接在偏滤器上的应用成为难点。本文基于钨铜梯度材料概念对钨、铜进行连接,以高活性Fe-Cu粉为中间层,在还原炉中采用扩散连接的方法对W-Cu复合材料与Cu进行连接,并对连接样品的金相显微形貌、显微硬度、拉伸强度和元素分布进行研究。结果表明,采用添加中间层的方法可以有效改善连接界面,提高连接质量。金相、显微硬度和能谱分析说明W-Cu与Cu连接样品的连接界面处形成了连续、紧密的结合;拉伸实验测得的平均强度为168.55 MPa,接近于Cu基材的强度,进一步证实添加中间层的方法可实现W-Cu与Cu的扩散连接。     

纳米Si粉对聚硅氧烷裂解及用其连接的SiC陶瓷接头强度的影响

无压烧结SiC(SSiC)陶瓷是重要的高温结构材料,连接技术是扩大其应用范围的关键技术之一。将纳米Si粉添加到聚硅氧烷(SR355)中制成连接材料,通过反应成形连接工艺连接SSiC。结果表明,纳米Si粉的加入对SR355的交联固化以及裂解和结晶化过程有一定的抑制作用,并能增加其陶瓷产率,因而可减少中间层的气孔率和收缩率,有利于连接强度的提高。纳米Si粉的最佳添加量为2%(质量分数)。连接温度对接头强度有显著影响,在纳米Si粉添加量为2%、连接压力为40 kPa、保温时间为30 min的条件下,当连接温度为1 100℃时,连接强度达到最大值64.7 MPa。微观结构研究显示,该试样中间层由C、O和Si元素组成,界面结合较好,Si和O元素在界面区域发生扩散,有利于提高连接强度。     

Effect of antibiotics of chemotaxis of human leukocytes

The effect of 20 different antibiotics on chemotaxis by human neutrophils was studied. Human leukocytes incubated with chloramphenicol, rifampin, sodium fusidate, and tetracyclines in vitro showed markedly depressed migration. The mechanisms by which these antibiotics affect leukotaxis are discussed.     

Quality of life of relatives of mental patients

Usage of quality of life of psychiatric patients' relatives as the parameter of estimation of the quality of psychiatric care is considered. By means of standard questionnaire elaborated by the authors as well as by means of both individual and group conversations the quality of life was analyzed in 40 relatives which lived together with psychiatric patients. Different spheres of their life and difficulties (financial, social-psychologic, production) were examined in families with such patients. The defects of psychiatric care that had direct influence on the quality of life of the psychiatric patients' relatives are outlined.     

转炉炉壳热应力分析

根据实际转炉建立实体模型。以有限元为手段,考虑了炉衬和炉壳材料的物性参数随温度变化的特点和炉衬与炉壳之间膨胀间隙,计算了转炉炉壳在温度载荷和炉衬膨胀压力同时作用下的热应力。所得结果可为转炉炉壳设计提供依据。     

The effect of amount of possession of the trait of hostility on accuracy of perception of hostility in others.

Some theories of personality hold that an individual's perception of others is influenced by his own personality characteristics; more specifically, that a trait of low social value will be projected more into others, and that insight into the possession of these characteristics reduces this distortion. These 2 hypotheses were tested by having a group of college students rate each other (including themselves) on degree of friendliness or hostility. Agreement with group rating about self yielded the insight score. In general, the hypotheses were supported; the "friendly" Ss were most accurate in their perception of others, and insight was positively associated with accurate perception. From Psyc Abstracts 36:04:4HL16M. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Comparison of rates of infection of two methods of emergency ventricular drainage

The rates of infection of two methods of external ventricular drainage in use at Atkinson Morley's Hospital--namely, (a) percutaneous drainage with Rickham reservoirs and (b) tunnelled ventriculostomies--were compared in this retrospective review. Percutaneous drainage of CSF with Rickham reservoirs was associated with a 27% rate of infection as identified by positive microbiological cultures; tunnelled ventriculostomy catheters had a 10% infection rate. The difference in the infection rate between the two methods was statistically significant (P < 0.015). Other variables examined, including the age and sex of the patients and the reasons for ventricular drainage, were not associated with an increased rate of infection. Most infections from either method were caused by a coagulase negative staphylococcus. The average duration of ventricular drainage before identification of positive cultures was 5.7 days for Rickham reservoirs and 6.0 days for ventriculostomies.     

浅析《野草》的版画特征

鲁迅先生一生热爱美术作品,对版画中木刻兴趣尤甚.<野草>作为其"写心之作",亦呈现出一些与木刻版画一致的审美特征:一是具有木刻版画的色彩特征,多对比、多冷色,有阴郁的美感;二是具有木刻版画的力度特征,环境描写、人物刻画处处刀锋毕现,遒劲有力,有一种"力之美".     

四辊破碎机车刀架的改造

针对四辊破碎机车刀架车削中存在的几个问题,详细介绍了电动车刀架的结构和工作原理,建立主要设计参数的数学表达式,并进行适当的分析。改造后,这种电动车刀架运行平稳、可靠、方便、省力,取得了预期的效果。