纳米Al2O3颗粒增强新型铜基自润滑复合材料

以Cu-Ni-Y₂O₃-MoS₂-Graphite混合粉为基体,加入质量分数分别为0%、1%、2%、3%、4%的纳米Al₂O₃增强相,采用粉末冶金方法制备纳米Al₂O₃增强新型铜基自润滑复合材料。结果表明：随着铜合金粉末中纳米Al₂O₃颗粒含量的增加 , 所制备自润滑复合材料样品的密度下降,但硬度和压溃强度先上升后下降,在Al₂O₃含量为2%时硬度从HV 23.7增加到HV 35.1,压溃强度从189 MPa提高到276 MPa。由石墨和MoS₂组成的混合固体自润滑材料的摩擦系数小且稳定,约0.12。Al₂O₃质量分数为2%的样品磨损量最小,是未加Al₂O₃试样磨损量的1/7～1/8。铜基体经过镍、纳米Al₂O₃等弥散颗粒强化和固体润滑相石墨和MoS₂的加入,所制备的材料已具有一定的自润滑性能。     

Al2O3颗粒增强纯铝基复合材料的研究

本文探讨了用粉末冶金法,采用常规的冶金加工设备和工艺,制造Al₂O₃颗粒增强纯铝基复合材料的可行性。研究了不同Al₂O₃体积含量复合材料的显微组织及力学性能。初步试验了二次热挤压变形对颗粒分布和对基体强化的影响。结果表明,Al₂O₃颗粒与纯铝粉混合,加压烧结制备的复合材料,组织致密,颗粒分布均匀,随Al₂O₃含量增加,复合材料强度、硬度及弹性模量大大提高,Al₂O₃含量小于10%时,塑性不降低。二次热挤压有助于提高颗粒分布的均匀性;并使基体显著强化。     

Al2O3-SiO2纤维增强ZL108合金复合材料的强度特性

用低成本的Al₂O₃-SiO₂系纤维作为增强相,通过加压铸造法制作ZL108合金复合材料,并对该复合材料和ZL108合金进行不同温度下的时效处理和压缩试验。通过DSC、EPMA和TEM分析认为:经488K、0.5h时效处理(T6处理)的V_f 20%的复合材料在573K以下的压缩屈服强度低于ZL108合金,是由于基体中的Mg与Al₂O₃-SiO₂纤维在加压铸造过程中起化学反应而生成MgAl₂O₄,损耗了基体中的大量Mg,导致基体铝合金时效硬化效果很差,所以压缩屈服强度低下。623K、720h保温后的V_f 20%的复合材料的压缩屈服强度比ZL108合金要高得多,是由于在这种温度环境下对ZL108合金来说是过时效,所以纤维的增强怍用显得明显。在高温(673K)下V_f 20%的复合材料的屈服强度比ZL108台金高一倍左右。不论在什么温度场合下V_f5%的复合材料的屈服强度比V_f 20%的复合材料都低。     

原位生成Al2O3/Cu复合材料的新工艺

采用一种新型工艺制备了Al₂O₃/Cu复合材料。高能球磨制备亚稳态的Cu-0.8 wt% Al合金粉,再将Cu₂O粉与其一起进行高能球磨,然后将复合粉末压坯在真空炉中同时进行氧化和烧结。该工艺省略了还原剩余Cu₂O的环节,氧化和烧结时间仅为1 h。生成的Al₂O₃的粒径约250nm,颗粒间距约500 nm,均匀弥散分布;该材料冷加工后性能接近SCM制品性能。该配比的Al₂O₃/Cu复合材料的热稳定性良好,在800℃下循环冷淬20次无裂纹;软化温度为700℃。     

Y2O3表面改性Al2O3P增强6061Al复合材料组织与性能

采用液相包裹法对Al₂O₃微粉进行稀土Y₂O₃表面改性,用挤压铸造法制备表面经稀土Y₂O₃改性的Al₂O_3P/6061Al复合材料,并对复合材料的显微组织及拉伸性能进行分析和研究。结果表明:表面经稀土Y₂O₃改性的Al₂O₃微粉能均匀的分布于基体中,界面润湿性得以改善,复合材料组织更加均匀。TEM观察表明:改性粉体在制备复合材料前后表面存在颗粒状包裹层。对其表面进行EDAX分析,结果显示含有Y,Al和O元素。粉体XRD图谱中有Y₂O₃衍射峰的存在。拉伸性能测试表明:改性粉体对Al合金增强效果明显增加,抗拉强度提高29.8％,屈服强度提高38.4％,延伸率提高10.3％。对拉伸断口进行SEM分析,改性后复合材料断口韧窝更加均匀、丰满,材料表现出良好的塑性。     

Al2O3/Al复合材料氧化生长的动力学研究

通过热重分析实验,研究了Al-Mg-Si合金熔体在高温空气气氛中直接氧化的孕育期与工艺温度及母合金中Mg、Si含量的关系,摸清了铝合金本体氧化的表观活化能与母合金Mg、Si含量的关系,证实了Al-Mg-Si合金直接氧化过程符合Arrhenius公式.     

片状Al2O3对Al2O3/FEP复合材料热导率的影响

通过混炼工艺制备了片状Al₂O₃填充聚全氟乙丙烯(FEP)复合材料,以颗粒状Al₂O₃为对比样品,研究了片状Al₂O₃形状和尺寸对 FEP基复合材料热导率的影响,利用SEM观察了FEP基复合材料的微观形貌。结果表明：在低填充量下,Al₂O₃颗粒在FEP基体中呈“海岛”状分布,没有形成连续的导热网链,但其热导率明显提高;复合材料拉伸强度与断裂伸长率随Al₂O₃含量的增加而减小;低填充量时复合材料热导率的提高主要来自Al₂O₃的微细片状结构,这种微细片状结构一方面提高了有效导热路径,另一方面增加了颗粒与基体之间接触面积,因此有利于热导率的提高。     

还原温度对纳米FeCo/Al2O3复合材料结构和磁性的影响

采用溶胶-凝胶法及在氢气中还原的工艺制备了纳米FeCo/Al₂O₃复合材料。利用X射线衍射、透射电镜、振动样品磁强计和Mssbauer谱学对样品微观结构和磁性进行了研究。结果表明：纳米FeCo/Al₂O₃复合材料中的FeCo合金为体心立方结构;随着还原温度的提高,α-FeCo合金晶粒尺寸变大,Al₂O₃的存在有效地抑制了α-FeCo合金晶粒的团聚和生长;随着α-FeCo合金晶粒尺寸的变大,样品的比饱和磁化强度增加,而矫顽力先增大后减小,两者分别在1100℃和1000℃时达到最大值62.41 emu·g-1和208.99Oe,FeCo/Al₂O₃由超顺磁和磁有序的混合状态转变为完全的磁有序状态;矫顽力的变化是由于FeCo合金的磁学结构由单磁畴结构转变为多磁畴结构造成的。     

ZA22/Al2O3复合材料切削加工表面质量的研究

采用硬质合金刀具研究了挤压铸造Al₂O₃短纤维强化ZA22合金复合材料的切削加工表面质量。发现在相同切削条件下,该复合材料表面质量优于ZA22合金。高的切削速度、低的进给量及低的切削深度有利于提高该复合材料的切削加工表面质量。随Al₂O₃纤维体积分数增大,复合材料切削加工表面粗糙度降低。     

Y2O3添加量对Al2O3/ZrO2共晶陶瓷显微组织及力学性能的影响

为探索第三组元Y₂O₃添加对Al₂O₃/ZrO₂共晶陶瓷显微组织与机械性能的影响,本文利用低温度梯度的高温熔凝法制备了直径为20 mm的Al₂O₃/ZrO₂(Y₂O₃)共晶陶瓷块体,采用SEM、EDS及XRD技术对共晶陶瓷进行微结构分析,并利用维氏压痕法对其硬度和断裂韧性进行测试。SEM结果表明,凝固组织由群集的共晶团结构组成,随着Y₂O₃添加量的增加,共晶团形态由胞状转变为枝晶状,内部相间距在1~2 μm范围内变化。力学测试表明,Y₂O₃摩尔分数小于1.1%时,由于组织内部存在低硬度m-ZrO₂及微裂纹缺陷,故陶瓷硬度较低,约为(9.53±0.22 )GPa;当Y₂O₃摩尔分数为1.1%时,陶瓷硬度最大,约为(18.05±0.27)GPa;当Y₂O₃的摩尔分数大于1.1%时,由于共晶团边界区内气孔缺陷及粗大组织增多,引起陶瓷硬度值略有下降。低Y₂O₃摩尔分数添加时,陶瓷断裂韧性相对较高,约为(6.30±0.16)MPa·m^1/2,这与其内部存在大量微裂纹缺陷有关;随着Y₂O₃添加量的增加,陶瓷的微裂纹数量减少、边界区内缺陷增多,断裂韧性降低。     

纳米Al2O3增强铝基复合材料的制备技术和发展方向

纳米颗粒具有极高的增强效率,能够显著提高铝基复合材料的综合性能.纳米Al2 O3/Al复合材料作为其中的代表,具有高弹性模量、高强度和低密度等优势,得到长期的关注和研究.详细介绍了纳米Al2O3/Al复合材料的制备方法,分析了各制备方法的优点和缺点,并对纳米Al2O3/Al复合材料的发展前景进行了展望.     

纳米Al2O3/聚醚砜-环氧树脂复合材料的介电性能及热稳定性能

本实验制备了纳米Al_2O_3/聚醚砜-环氧树脂复合材料,考察了不同纳米氧化铝和聚醚砜的用量对复合体系力学和介电性能的影响,并对其热稳定性能进行了研究。结果表明:当添加1phr纳米氧化铝(Nano-Al_2O_3)和5phr聚醚砜(PES)时,三元复合材料EP/5PES/1Al_2O_3的拉伸强度提高到58 MPa,断裂伸长率达到13%,冲击强度达到16.2kJ/m~2,相比纯环氧树脂分别提高了61.1%、20.3%和8.0%。而且在100Hz的室温测试条件下,EP/5PES/1Al_2O_3材料的介电常数和介电损耗分别达到7.6和0.016,较纯环氧树脂均有一定幅度的增加。热重分析(TG)结果表明,EP/5PES/1Al_2O_3复合材料的初始分解温度为358℃,比纯环氧树脂提高了14℃,说明热稳定性有较大幅度的提高。     

纳米-Al2O3/SiO2加入量对MgO-Al2O3-SiO2复相陶瓷烧结机理的影响

为了探究纳米-Al₂O₃/SiO₂加入量对MgO-Al₂O₃-SiO₂复相陶瓷烧结行为的作用机理。以微米级MgO、纳米级Al₂O₃和SiO₂为主要原料制备陶瓷基复合材料。通过XRD和 SEM等检测手段对烧后试样的物相组成和微观结构进行测试与表征,重点研究Al₂O₃/SiO₂的加入对复相陶瓷物相组成、微观结构及烧结性能的影响。结果表明:随着Al₂O₃/SiO₂加入量的增大,试样烧后相对密度和烧后线变化率呈先增大后减小再增大的趋势,加入15%Al₂O₃/SiO₂(质量分数)的试样经1 500 ℃烧结后,其相对密度可以达到94%。引入的Al₂O₃/SiO₂与基体中的MgO生成镁铝尖晶石与镁橄榄石相,原位反应伴随的体积膨胀,抵消部分烧结过程中的体积收缩。Al₂O₃/SiO₂加入量为75%(质量分数)的试样经1 400 ℃烧结后,基体中有大量堇青石相生成,随着煅烧温度提高到1 500 ℃,堇青石分解所产生的高温液相促进了试样的烧结收缩。     

Ozone sensing using In2O3-modified Ga2O3 thin films

It is shown that at elevated temperatures the conductance of an In ₂O₃-modified Ga₂O₃ thin film depends significantly and reversibly on the ozone concentration in the ambient air. This ozone sensitivity is much greater than with pure Ga ₂O₃ or In₂O₃ thin films, respectively. The ozone sensitivity of the In₂O₃-modified Ga₂O₃ thin film is characterized by an impressive selectivity, and is maximal at an operation temperature of about 600°C. The cross sensitivities to other gases present in ambient conditions are small compared to the ozone sensitivity, thus opening the way to use this system for ambient ozone monitoring. The results are discussed using an electron injection model     

Preparation and oxidation of an Al2O3-modified aluminide coating

An Al₂O₃-modified aluminide coating was produced by aluminizing an as-electrodeposited Ni-Al₂O₃ nanocomposite film using pack cementation method at 1100  C for 4 h. For comparison, aluminizing was also performed in the same condition on an as-deposited Ni film without Al₂O₃ nanoparticles. SEM/EDAX and TEM results indicated that the co-deposited Al₂O₃ nanoparticles were homogeneously dispersed in the finer-grain nanocrystalline Ni grains. The isothermal and cyclic oxidation in air at 900 °C indicated that the Al₂O₃-modified aluminide coatings were profoundly oxidation resistant as compared to the Al₂O₃-free aluminide coatings due to the faster formation of a continuous adherent α-Al₂O₃ scale. The effect of Al₂O₃ on the microstructure and the oxidation of the aluminide coating are discussed in the detail.     

纤维预热温度对连续Al2O3f/Al复合材料力学性能的影响

选用Nextel610型Al₂O₃纤维为增强体、ZL210A连续氧化铝合金为基体,采用真空压力浸渗法制备纤维增强铝基复合材料(Al₂O_3f/Al),纤维的体积分数为40%,预热温度分别为500、530、560和600℃,研究了纤维预热温度对Al₂O_3f/Al复合材料的微观组织、纤维损伤和力学性能的影响。结果表明：随着纤维预热温度的提高复合材料的致密度随之提高,最大达到99.2%,材料的组织缺陷最少,纤维的分布均匀;随着纤维预热温度的提高从复合材料中萃取出来的Al₂O₃纤维的拉伸强度不断降低,纤维预热温度为600℃的复合材料中Al₂O₃纤维的拉伸强度仅为1150 MPa,纤维表面粗糙,有大尺寸附着物。纤维的预热温度对Al₂O_3f/Al复合材料的拉伸强度有显著的影响。预热温度为500、530、560和600℃的复合材料其拉伸强度分别对应于298、465、498和452 MPa。组织缺陷、纤维损伤和界面结合强度,是影响连续Al₂O_3f/Al复合材料强度的主要因素。     

原位自生纳米Al2O3/Al-Zn-Cu复合材料的力学性能

将纳米ZnO粉末和Al粉球磨后冷压成Al-ZnO预制块,然后将其加到Al-Zn-Cu熔体中进行Al-ZnO原位反应,制备出纳米Al₂O₃颗粒增强Al-Zn-Cu基复合材料。能谱面扫描分析和透射电镜观察结果表明,复合材料由纳米Al₂O₃颗粒和Al₂Cu析出相两种颗粒/析出相组成。纳米Al₂O₃颗粒通过异质形核和晶界钉扎,细化了Al-Zn-Cu合金晶粒组织和Al₂Cu析出相。原位纳米Al₂O₃颗粒的生成提高了基体合金的拉伸性能,轧制+热处理使Al₂O₃/Al-Zn-Cu复合材料的拉伸强度比相同处理的基体合金提高约100%,总伸长率提高约98%。     

Properties and Structures of Bi2O3-B2O3-TeO2 Glass

Glass formation range of Bi₂O₃—B₂O₃—TeO₂ system has been investigated（B₂O₃ < 40 mol%）.Four glasses with compositions xBi₂O₃—3OB₂O₃—（70—x）TeO₂（x = 40,50,60 and 70 mol%） have been prepared by using melt quenching technique.The effect of Bi₂O₃ content on thermal stability,optical properties and structures of these four Bi₂O₃—B₂O₃—TeO₂ glasses is systematically investigated by inductive coupled plasma emission spectrometer（ICP）,differential scanning calorimetry（DSC）,Raman spectra and X-ray photoelectron spectroscopy（XPS）.It is found that the density,refractive index and optical basicity increase with increasing Bi₂O₃.The Raman spectra and XPS spectra show that the glass network is mainly constituted by the[BiO₆] octahedron,[TeO₄]trigonal bipyramidal,[TeO₃]trigonal pyramid,[BO₃]trigonal pyramid and[BO₄]tetrahedron structural units.With increasing Bi₂O₃,the coordination number around B atom changes from 3 to 4 and [TeO₄]units are converted to[TeO₃]units.Bi⁵⁺ ions may exist in Bi₂O₃—B₂O₃—TeO₂（BBT） system and their amount grows with increasing Bi₂O₃ content.     

Nano-Al2O3 multilayer film deposition on cotton fabrics by layer-by-layer deposition method

Al₂O₃ nanoparticles were used for fabrication of multilayer nanocomposite film deposition on cationic cotton fabrics by electrostatic self-assembly to improve the mechanical, UV-protection and flame retardancy properties of cotton fabrics. Cotton fabric surface was modified with a chemical reaction to build-up cationic charge known as cationization. Attenuated Total Reflectance Fourier Transform Infrared Spectroscopy, X-ray Photoelectron Spectroscopy and Scanning Electron Microscopy were used to verify the presence of deposited nanolayers. Air permeability, whiteness value, tensile strength, UV-transmittance and Limited Oxygen Index properties of cotton fabrics were analyzed before and after the treatment of Al₂O₃ nanoparticles by electrostatic self-assemblies. It was proved that the flame retardancy, tensile strength and UV-transmittance of cotton fabrics can be improved by Al₂O₃ nanoparticle additive through electrostatic self-assembly process.     

A12O3陶瓷复合材料的研究进展

介绍了Al2O3陶瓷增韧技术和A12O3陶瓷增强金属基复合材料的研究进展,指出复合增韧是未来A12O3认陶瓷增韧技术的发展方向;金属表面自生Al2O3防护层技术是提高金属耐蚀性,降低成本的有效方法;三维网络Al2O3陶瓷/金属复合材料具有更优良的力学性能;仿生设计和计算机模拟技术是开发新型网络Al2O3陶瓷骨架的重要手...