| TC32钛合金不同热处理工艺下的组织性能及断裂机制 |
| |
| 引用本文： | 李明兵,王新南,商国强,祝力伟,李静,李星,朱知寿. TC32钛合金不同热处理工艺下的组织性能及断裂机制[J]. 金属热处理, 2021, 46(4): 112-117. DOI: 10.13251/j.issn.0254-6051.2021.04.019 |
| |
| 作者姓名： | 李明兵 王新南 商国强 祝力伟 李静 李星 朱知寿 |
| |
| 作者单位： | 中国航空发动机集团 北京航空材料研究院 先进钛合金重点实验室, 北京 100095 |
| |
| 摘 要： | 以新型高性能低成本TC32钛合金为研究对象,通过光学显微镜、扫描电镜、透射电镜和拉伸试验机等,研究了普通退火(700℃ ×2 h,AC)和双重退火(880℃ ×2 h,AC+550℃ ×6 h,AC)两种热处理工艺对该合金显微组织和力学性能的影响.结果表明:普通退火后,TC32合金组织中初生α相含量约为37.2％,并产...
|
| 关 键 词： | TC32钛合金 热处理 显微组织 力学性能 断裂机制 |
| 收稿时间： | 2020-10-05 |
Microstructure,mechanical properties and fracture mechanism of TC32 titanium alloy with different heat treatment processes |
| |
| Li Mingbing,Wang Xinnan,Shang Guoqiang,Zhu Liwei,Li Jing,Li Xing,Zhu Zhishou. Microstructure,mechanical properties and fracture mechanism of TC32 titanium alloy with different heat treatment processes[J]. Heat Treatment of Metals, 2021, 46(4): 112-117. DOI: 10.13251/j.issn.0254-6051.2021.04.019 |
| |
| Authors: | Li Mingbing Wang Xinnan Shang Guoqiang Zhu Liwei Li Jing Li Xing Zhu Zhishou |
| |
| Affiliation: | Key Laboratory of Advanced Titanium Alloys, Beijing Institute of Aeronautical Materials, Aero Engine Corporation of China, Beijing 100095, China |
| |
| Abstract: | Effect of two heat treatment processes, which were normal annealed (700 ℃ for 2 h, AC) and double annealed (880 ℃ for 2 h, AC and 550 ℃ for 6 h, AC), on microstructure and mechanical properties of the new high-performance and low-cost TC32 titanium alloy was studied by using optical microscope (OM), scanning electron microscope (SEM), transmission electron microscope (TEM), and tensile testing machine. The results show that after normal annealing, the content of primary α phase is about 37.2%, and a slight spheroidization occurres, the β-transformed matrix is composed of coarser lamellar secondary α phase and residual β phase. The average ultimate strength (UTS) under this process is 939 MPa, and the average elongation (EL) is 17.4%. After double annealing, volume fraction of primary α phase which occurred recrystallization is about 11.8%, and β-transformed matrix is composed of fine lamellar secondary α phase with weaving basket-weave structures. The average ultimate strength (UTS) under this process is 1258 MPa, and the average elongation (EL) is 9.4%. Fracture morphologies show that the tensile fracture mechanism of both processes belongs to ductile fracture. The fracture characteristics of normal annealed have larger fibrous and shear lip zones, no obvious radical zone, and more equiaxed dimples with larger in size and deeper in depth. The fracture characteristics of double annealed have a certain area of radical zone, in addition to the equiaxed dimples, a number of tearing edges is observed. |
| |
| Keywords: | TC32 titanium alloy heat treatment microstructure mechanical properties fracture mechanism |