| 高熔点稀土倍半氧化钪(Sc2O3)晶体的生长 |
| |
| 引用本文： | 赵衡煜,侯文涛,薛艳艳,王庆国,董建树,雷震霖,徐晓东,徐军.高熔点稀土倍半氧化钪(Sc2O3)晶体的生长[J].人工晶体学报,2021,50(4):732-734. |
| |
| 作者姓名： | 赵衡煜 侯文涛 薛艳艳 王庆国 董建树 雷震霖 徐晓东 徐军 |
| |
| 作者单位： | 1.同济大学物理科学与工程学院,上海 200092;2.中国科学院沈阳科学仪器股份有限公司,沈阳 110179;3.江苏师范大学物理与电子工程学院,徐州 221116 |
| |
| 基金项目： | 国家重点研发计划(2016YFB1102202);国家自然科学基金(61621001,51672190) |
| |
| 摘 要： | 本文通过自主研发制造新型高温晶体生长炉,并采用热交换-温度梯度法的热场结构,从而克服了高温环境下坩埚污染。调节热场结构并引入循环气,增大了温度梯度并改善了结晶驱动力不足的问题。用热交换-温度梯度法生长了2英寸(1英寸=2.54 cm)级的氧化钪(Sc2O3)晶体,这一结果是目前已知的最大尺寸的倍半氧化物单晶。氧化钪晶体呈现无色透明,外形完整、内部无气泡或其他可观察到的宏观缺陷。尺寸为φ55 mm×50 mm。其中放肩部分高度15 mm,等径生长部分的高度为40 mm。块状晶体的XRD谱只有(222)与(444)峰,可判定为单晶体,双晶摇摆曲线半高宽(FWHM)为113″,显示较好的结晶性能。
|
| 关 键 词： | 氧化钪晶体 倍半氧化物晶体 热交换法 温度梯度法 |
| 收稿时间： | 2021-03-26 |
Growth of High Melting Point Rare Earth Sesquioxide Scandium Oxide Crystal (Sc2O3) |
| |
| ZHAO Hengyu,HOU Wentao,XUE Yanyan,WANG Qingguo,DONG Jianshu,LEI Zhenlin,XU Xiaodong,XU Jun.Growth of High Melting Point Rare Earth Sesquioxide Scandium Oxide Crystal (Sc2O3)[J].Journal of Synthetic Crystals,2021,50(4):732-734. |
| |
| Authors: | ZHAO Hengyu HOU Wentao XUE Yanyan WANG Qingguo DONG Jianshu LEI Zhenlin XU Xiaodong XU Jun |
| |
| Affiliation: | 1. School of Physics Science and Engineering, Tongji University, Shanghai 200092, China;2. SKY Technology Development Co., Ltd., Chinese Academy of Sciences, Shenyang 110179, China;3. School of Physics and Electronic Engineering, Jiangsu Normal University, Xuzhou 221116, China |
| |
| Abstract: | A new type of high temperature crystal growth furnace has been designed and fabricated with the structure of heat-exchange method (HEM) combined with temperature gradient technique (TGT). Such design could solve the problem of crucible pollution at high temperature and the insufficiency of crystal driving force that derived from distribution of heat. 2 inch Sc2O3 crystal is grown and presented in this work, which is recognized as the largest sesquioxide crystal in size. The Sc2O3 crystal is colorless and transparent with no crack on the surface and no bubbles or other macro-defects inside of the bulk. The size of bulk Sc2O3 crystal is measured to be φ55 mm×50 mm, 40 mm of which is in equal-diameter growth while the rest 15 mm belongs to shouldering part. (222) and (444) peaks are observed in the the XRD pattern of bulk Sc2O3 crystal, which indicates to be single phase. X-ray rocking curve (RC) shows good crystalline quality and FWHM of RC peak at 15.76° is determined to be 113″. |
| |
| Keywords: | Sc2O3 crystal sesquioxide crystal heat exchange method temperature gradient technique |
| 本文献已被 CNKI 等数据库收录！ |
| 点击此处可从《人工晶体学报》浏览原始摘要信息 |
|
点击此处可从《人工晶体学报》下载全文 |
|