| 不同热处理状态AMS6308钢惯性摩擦焊接头组织及力学性能 |
| |
| 引用本文： | 张春波,周军,赵玉珊,安洪亮. 不同热处理状态AMS6308钢惯性摩擦焊接头组织及力学性能[J]. 焊接学报, 2015, 36(7): 21-24 |
| |
| 作者姓名： | 张春波 周军 赵玉珊 安洪亮 |
| |
| 作者单位： | 机械科学研究院 哈尔滨焊接研究所, 哈尔滨 150028 |
| |
| 基金项目： | 国家自然科学基金资助项目(51475196,51075174) |
| |
| 摘 要： | 在HWI-IFW-130型轴/径向多功能惯性摩擦焊机上,成功实现热轧态与热轧态AMS6308钢、淬火+回火态与淬火+回火态AMS6308钢惯性摩擦焊接. 对两种不同热处理状态的焊接接头进行检测分析. 结果表明,母材为热轧态的焊接接头,焊缝区为马氏体组织,热力影响区和热影响区为马氏体+贝氏体组织;母材为淬火+回火态的焊接接头,焊缝区为马氏体组织,热力影响区和热影响区为马氏体回火组织. 以焊缝为中心,显微维氏硬度呈对称分布,焊缝区显微维氏硬度最高;两种不同热处理状态母材获得的焊接接头,拉伸均断于母材.
|
| 关 键 词： | 惯性摩擦焊 AMS6308钢 航空齿轮 |
| 收稿时间： | 2015-01-01 |
Microstructure and mechanical properties of inertia friction welding joint of AMS6308 steel at different heat treatment state |
| |
| ZHANG Chunbo,ZHOU Jun,ZHAO Yushan and AN Hongliang. Microstructure and mechanical properties of inertia friction welding joint of AMS6308 steel at different heat treatment state[J]. Transactions of The China Welding Institution, 2015, 36(7): 21-24 |
| |
| Authors: | ZHANG Chunbo ZHOU Jun ZHAO Yushan AN Hongliang |
| |
| Affiliation: | Harbin Welding Institute, China Academy of Machinery Science & Technology, Harbin 150028, China |
| |
| Abstract: | Hot-rolled AMS6308 steel and Q-tempered AMS6308 steel were welded on HWI-IFW-130 inertia friction welding machine, respectively. Mechanical properties and microstructures of joints were studied. For the joint welded by hot-rolled AMS6308 steel, weld zone is martensite microstructure, heat affected zone and thermo-mechanically affected zone are martensite and bainite microstructures. For the joint welded by Q-tempered AMS6308 steel, the microstructure of weld zone is the same with that by hot-rolled AMS6308 steel, while the microstructure in heat affected zone and thermo-mechanically affected zone are tempered martensite. The microhardness distribution of the joint is symmetrical with the center of weld, and the highest microhardness occurs in weld zone. All fractures occur at the base metal in tensile test. |
| |
| Keywords: | inertia friction welding AMS6308 steel aviation gear |