摘 要: | Ho3+/Yb3+co-doped Li YF4 single crystals with various Yb3+concentrations and ~ 0.98 mol% Ho3+concentration are grown by the Bridgman method under the conditions of taking Li F and YF3 as raw materials and a temperature gradient(40°C/cm–50°C/cm) for the solid–liquid interface.The luminescent performances of the crystals are investigated through emission spectra,infrared transmittance spectrum,emission cross section,and decay curves under excitation by 980 nm.Compared with the Ho3+single-doped Li YF4 crystal,the Ho3+/Yb3+co-doped Li YF4 single crystal has an obviously enhanced emission band from 1850 nm to 2150 nm observed when excited by a 980-nm diode laser.The energy transfer from Yb3+to Ho3+and the optimum fluorescence emission around 2.0 μm of Ho3+ions are investigated.The maximum emission cross section of the above sample at 2.0 μm is calculated to be 1.08×10-20cm2 for the Li YF4 single crystal of1-mol% Ho3+and 6-mol% Yb3+according to the measured absorption spectrum.The high energy transfer efficiency of88.9% from Yb3+to Ho3+ion in the sample co-doped by Ho3+(1 mol%) and Yb3+(8 mol%) demonstrates that the Yb3+ions can efficiently sensitize the Ho3+ions.
|