| 聚马来酸防皱整理剂的合成与应用 |
| |
| 引用本文： | 陈明珍,陆必泰.聚马来酸防皱整理剂的合成与应用[J].印染助剂,2001,18(3):12-14. |
| |
| 作者姓名： | 陈明珍 陆必泰 |
| |
| 作者单位： | 武汉科技学院 |
| |
| 摘 要： | 通过L9(34)正交试验,选择具有合适分子量的聚马来酸(PMA)无醛防皱整理剂和最优防皱整理工艺.并对棉织物进行防皱整理,获得良好的防皱整理效果,WRA值可达到243.5°,断裂强度保留率在70%以上.同时优选出合成PMA的最佳条件.
|
| 关 键 词： | 聚马来酸 防皱整理剂 合成 分子量 扩皱回复角 应用 |
| 文章编号： | 1004-0439(2001)03-0012-03 |
| 修稿时间： | 2000年12月4日 |
White Discharge Printing of Artificial Fur with Reduetant |
| |
| CHEN Ming_zhen,LU Bi_tai.White Discharge Printing of Artificial Fur with Reduetant[J].Textile Auxiliaries,2001,18(3):12-14. |
| |
| Authors: | CHEN Ming_zhen LU Bi_tai |
| |
| Abstract: | Through L9(34) orthogonal test, non-formaldehyde crease proofing agent polymaleic acid (PMA) with proper molecular weight and the optimal anti-crease finishing process were selected. The cotton fabric treated with this agent had got good wrinkle resistant result with WRA up to 243.5 and retained breaking strength more than 70%. Furthermore, synthetic process of PMA were optimized. |
| |
| Keywords: | polymaleic acid crease proofing agent synthesis molecular weight wrinkle recovery angle(WRA) |
| 本文献已被 CNKI 万方数据 等数据库收录！ |