中低温环氧树脂修井液

石油天然气的消耗量急剧增加，同时伴随着常规油气井开发的减少，非常规油气井，如深井、海洋井、页岩气井等的开发迫在眉睫。这些复杂地质环境都有极大可能破坏水泥环的密封完整性，形成环空窜流，对生产造成阻碍和危险，产生极大的经济损失。环氧树脂体系可以作为一种修井液来代替水泥浆进行修井工作，解决水泥浆无法渗透入微小孔隙的缺陷。目前环氧树脂修井液体系配方繁多，普适性差，为同时满足不同温度地层的修井需求，便于现场施工的运输、存储和调配，提高修井经济性和推动工业化进程，设计了以液态芳香胺（LAA）为主要固化剂的体系。进行了组分优选和性能评价，对稠化性能、动力学和固化物的抗压强度和微观形貌进行了表征。结果表明，LAA体系初始稠度小于30 Bc，稠化时间在2～5 h之间可调，抗压强度在不同温度下都高于20 MPa，可以满足30～90 ℃普适性的修井需要。 

A Medium-Low Temperature Epoxy Based Workover Fluid

Presently the consumption of oil and natural gas has increased sharply, while the development of conventional oil and gas is reducing, this makes the development of unconventional oil and gas, such as oil and gas from deep wells, offshore wells and shale gas wells more and more imminent. In the development of unconventional oil and gas, the sealing integrity of cement sheath may probably be damaged, leading to oil and gas channeling in the annulus which imposes great hindrances and risks to oil and gas production and causes great economic losses. Epoxy based workover fluid can be used to replace cement slurry in workover job to solve the problem of inability of cement slurries to penetrate micro pores. Epoxy based workover fluids have many compositions and poor adaptability. To simultaneously satisfy the needs of workover operation in different formations with different temperatures, facilitate the transportation, storage and deployment of field operation, and improve the economy of workover and promote the industrialization process, a workover fluid was developed with liquid aromatic amine (LAA) as the main curing agent. The performance of the workover fluid was evaluated, the thickening performance and the kinetics of the workover fluid, and the compressive strength and micromorphology of the set product were characterized. The results show that the LAA system has initial consistency of less than 30 Bc, thickening time that is adjustable between 2 h and 5 h, compressive strength that is greater than 20 MPa at various temperatures, and it is able to satisfy the needs of workover operation at temperatures between 30 ℃ and 90 ℃.