Predictive environmental hydrogen embrittlement on fracture toughness of commercial ferritic steels with hydrogen-modified fracture strain model |
| |
Affiliation: | School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai, 200237, PR China |
| |
Abstract: | In this work, a practical numerical model with few parameters was proposed for the prediction of environmental hydrogen embrittlement. The proposed method adopts hydrogen enhanced plasticity-based mechanism in a fracture strain model to describe hydrogen embrittlement. Fracture toughness degradation of three commercial steels SA372J70, AISI4130 and X80 in high pressure hydrogen environment were investigated. Firstly, governing equations for hydrogen distribution and material damage evolution was established. Hydrogen enhanced localized flow softening effect was coupled within fracture strain dependency on stress triaxiality. Then, the numerical implementation and identification process of model parameters was described. Model parameters of the investigated steels were determined based on experiment results from literatures. Finally, with the calibrated model, fracture toughness reduction of the steels was predicted in a wide range of hydrogen pressure. The prediction results were compared with experimental results. Reasonable accuracy was reached. The proposed method is an attempt to reach balance between physical accurate prediction and engineering practicality. It is promising to provide a simplified numerical tool for the design and fit for service evaluation of hydrogen storage vessels. |
| |
Keywords: | Hydrogen embrittlement Fracture strain Fracture toughness Numerical prediction CrMo steel |
本文献已被 ScienceDirect 等数据库收录! |
|