Hydrogenation process in multiphase alloys of Ti-Zr-Mn-V system on the example of Ti42.75Zr27Mn20.25V10 alloy

The influence of phase composition and microstructure of Ti_42.75Zr₂₇Mn_20.25V₁₀ alloy on its hydrogenation kinetic and phase composition of hydrogenated product was studied. It is established that the process of dissociation of hydrogen molecules begins on the surface of Laves phase crystallites. The dissolution of atomic hydrogen in the material volume leads to the formation of cracks in the intermetallic crystallites, which further appear as additional centers of dissociation of hydrogen molecules and noticeably accelerate the diffusion of hydrogen into the bulk material. It was shown that the Laves phase acts as a donor of atomic hydrogen for the BCC solid solution during hydrogenation of two-phase structure, initiating intensive hydrogenation of the BCC phase at room temperature.