SiC纤维增强钛基复合材料的横向力学性能

采用十字形试样测试分析有C涂层和无C涂层两种SiC纤维增强钛基复合材料的横向力学性能,以横向载荷作用下应力-应变曲线上的非线性拐点计算界面的强度.结果表明,有C涂层的界面横向开裂强度为53 MPa,低于无C涂层的界面开裂强度196 MPa,并且前者在横向载荷作用下沿C涂层与纤维之间开裂,而后者沿反应生成物与基体间开裂;体积分数为30%的多根纤维钛基复合材料的非线性拐点应力低于单根纤维复合材料,这主要是由于残余应力的减少引起,界面强度并没有明显变化.

Transverse Mechanical Properties of Continuous SiC Fiber Reinforced Titanium Matrix Composites

Transverse mechanical properties of TMCs reinforced by two types of SiC fibers with and without C coating were determined by use of cross-shaped specimens. The initial nonlinear stress of the stress-strain curve under the applied transverse tensile load was adopted to calculate the interface strength. The interface strength with C coating was 53 MPa which was lower than 196 MPa of the one without C coating. The debonding position of two interface were different, i.e. the former was between the fiber and C c...