| 摘 要： | This paper reported an effectiveness of pre-cold rolling-induced{332}\113twins combined with subsequent isothermal x-phase formation for enhancement of uniform elongation in a b-type Ti–15Mo alloy with high yield strength level.Mechanical{332}\113twins were induced by cold rolling with an thickness reduction of 5%,which had little effect on x-phase precipitation after aging at 573 K for 3.6 ks.Twinning after the cold rolling was further activated during tensile deformation,even with the presence of isothermal x-phase.This combination of twins and x-phase enhanced uniform elongation from 0 to 9%at yield strength level of 890 MPa.The high yield strength was mainly dominated by dislocation slip due to the isothermal x-phase formation,and early onset of plastic instability after yielding was hindered due to the pre-cold rolling-induced twins.Dynamic microstructural refinement was induced by further twinning activation during deformation,which resulted in high work hardening rate corresponding enhancement of uniform elongation.
|