| Microstructure and properties of unleaded free-cutting brass containing stibium |
| |
| 作者姓名： | 肖来荣 舒学鹏 易丹青 张喜民 覃静丽 胡加瑞 |
| |
| 作者单位： | [1]School of Materials Science and Engineering, Central South University, Changsha 410083, China [2]The Key Laboratory of Non-ferrous Metals, Materials Science and Engineering, Ministry of Education; Changsha 410083; China |
| |
| 基金项目： | Projects （2006BRE03B02） supported by the Key Project of 11th Five-Year Plan of China |
| |
| 摘 要： | A new environmental friendly cutting brass containing stibium instead of lead was produced by casting and rolling. The microstructure was observed and the mechanical, dezincification and cutting properties were studied. The results show that the white particles distribute in both grains and grain boundaries, and the particles are mainly intermetallics containing stibium. The tensile strength, yield strength and elongation percentage of half-hard Sb-brass is 461.72 MPa, 213.3 MPa and 15.67%, respectively. Corresponding to HPb59-1 by the size as well as appearance of the chips and the mechanism of free-cutting, the cutting property of unleaded free-cutting Sb-brass is excellent. The unleaded Sb-brass has excellent dezincification corrosion resistance, and the average depth of longitudinal section is about 295.4 μm, while the average depth of lateral section is about 214.7 μm, and it is feasible to develop a new unleaded free-cutting Sb-brass.
|
| 关 键 词： | 无铅易切黄铜 锑 微观结构 性能 |
| 收稿时间： | 2007-07-15 |
| 修稿时间： | 2007-09-10 |
Microstructure and properties of unleaded free-cutting brass containing stibium |
| |
| XIAO Lai-rong, SHU Xue-peng, YI Dan-qing, ZHANG Xi-min, QN Jing-li, HU Jia-rui.Microstructure and properties of unleaded free-cutting brass containing stibium[J].Transactions of Nonferrous Metals Society of China,2007,17(A02):1055-1059. |
| |
| Authors: | XIAO Lai-rong SHU Xue-peng YI Dan-qing ZHANG Xi-min QN Jing-li HU Jia-rui |
| |
| Affiliation: | XIAO Lai-rong, SHU Xue-peng, YI Dan-qing, ZHANG Xi-min, Q1N Jing-li, HU Jia-rui |
| |
| Abstract: | |
| |
| Keywords: | nonleaded free-cutting brass stibium microstructure property |