Texture and magnetic properties of electrodeposited FePd films |
| |
Authors: | Hung-Pin Lin Jui-Chao Kuo |
| |
Affiliation: | 1. School of Electronic Science & Engineering, Nanjing University, Nanjing 210046, China;2. Department of Physics, Southeast University, Nanjing 210096, China;1. Institute of Magnetism, National Academy of Sciences of Ukraine and Ministry of Education and Science of Ukraine, Vernadsky Blvd. 36b, 03142, Kyiv, Ukraine;2. National Technical University of Ukraine “Igor Sikorsky Kyiv Polytechnic Institute”, Peremohy Ave. 37, 03056, Kyiv, Ukraine;1. Department of Physics, Shanghai Normal University, Shanghai 200234, China;2. Department of Materials Science and Engineering, Kyushu University, Fukuoka 819-0395, Japan;3. Synchrotron Light Application Center, Department of Electrical and Electronic Engineering, Saga University, Saga 840-8502, Japan;1. IFEG-CONICET en la Famaf-Unc, Medina Allende s/n, 5016 Córdoba, Argentina;2. Facultad de Ciencias Exactas y Naturales- UNCa- Av Belgrano. Catamarca, Argentina;1. Organic Chemistry Department, Campus de Excelencia Internacional CeiA3, University of Córdoba, Campus de Rabanales, Marie Curie Building, E-14014 Córdoba, Spain;2. KTH (Royal Institute of Technology), Chemical Technology, Teknikringen 42, SE-100 44 Stockholm, Sweden;1. Division of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081, PR China;2. Department of Physics, Capital Normal University, Beijing 100048, PR China |
| |
Abstract: | FePd films were deposited on brass substrates through electrodeposition using an alkaline electrolyte, which were annealed at 500, 600, and 700 °C for 1 h to form the ordered γ1-FePd fct phase. After annealing, the γ1-FePd fct phase is observed at 500, 600 and 700 °C. FePd films show the normal direction close to <101>, <111> and <421> directions after annealing 500, 600 and 700 °C, respectively. After annealing 500, 600 and 700 °C the average area grain size is 0.28 μm, 0.37 μm and 1.22 μm, respectively. The maximum coercivity Hc of 309 Oe observed at 500 °C can be explained with both effects of the <001> easy axis and the small grain size. |
| |
Keywords: | |
本文献已被 ScienceDirect 等数据库收录! |
|