Effects of borosilicate glass addition on the structure and dielectric properties of ZnTiO3 ceramics |
|
| Authors: | Yin-Lai Chai Yu-Jen Hsiao |
| Affiliation: | a Department of Resources Engineering, Dahan Institute of Technology, Hualien 971, Taiwan b Institute of Electro-Optical and Materials Science, National Formosa University, Huwei, Yunlin 632, Taiwan c Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan |
| Abstract: | ZnTiO3 powders and borosilicate glass were made by sol-gel method, and then mixed for co-firing at low temperatures. The results show that the borosilicate glass was liquefied to improve the density of the ceramic during sintering. However, Zn4O(BO2)6 and TiO2 were formed if too much borosilicate glass was added (over 10 wt.%). The microwave dielectric properties of the ZnTiO3 co-fired with borosilicate glass were also improved dramatically. With 5 wt.% borosilicate glass addition, ZnTiO3 ceramics can be sintered at 850 °C and shows excellent microwave properties: 22.2 for dielectric constant, and 52,460 for Q × f value at a frequency of 6 GHz. |
| Keywords: | A Oxides B Chemical synthesis C X-ray diffraction D Crystal structure |
| 本文献已被 ScienceDirect 等数据库收录！ | |