ZrB2–SiC laminated ceramic composites |
| |
| Authors: | Zhihui Lü Dongliang Jiang Jingxian Zhang Qingling Lin Zhengren Huang |
| |
| Affiliation: | 1. Key Laboratory of High-speed Railway Engineering of the Ministry of Education, Chengdu 610031, China;2. School of Civil Engineering, Southwest Jiaotong University, Chengdu 610031, China |
| |
| Abstract: | The oxidation behavior for ZrB2–20 vol% SiC (ZS20) and ZrB2–30 vol% SiC (ZS30) ceramics at 1500 °C was evaluated by weight gain measurements and cross-sectional microstructure analysis. Based on the oxidation results, laminated ZrB2–30 vol% SiC (ZS30)/ZrB2–25 vol% SiC (ZS25)/ZrB2–30 vol% SiC (ZS30) symmetric structure with ZS30 as the outer layer were prepared. The influence of thermal residual stress and the layer thickness ratio of outer and inner layer on the mechanical properties of ZS30/ZS25/ZS30 composites were studied. It was found that higher surface compressive stress resulted in higher flexural strength. The fracture toughness of ZS30/ZS25/ZS30 laminates was found to reach to 10.73 MPa m1/2 at the layer thickness ratio of 0.5, which was almost 2 times that of ZS30 monolithic ceramics. |
| |
| Keywords: | |
| 本文献已被 ScienceDirect 等数据库收录！ |
|