PMMA composites of single‐walled carbon nanotubes‐graft‐PMMA

To facilitate the dispersion of single‐walled carbon nanotubes (SWCNT) into poly(methyl methacrylate) (PMMA), SWCNT were functionalized with a RAFT chain transfer agent, and PMMA was grafted from the SWCNT by reversible addition–fragmentation transfer (RAFT) polymerization to give SWCNT‐g‐PMMA containing 6 wt % PMMA. SWCNT‐g‐PMMA in the form of small bundles was dispersed into PMMA matrices. The SWCNT‐g‐PMMA filler increased the glass transition temperature (T_g) of the composite when the matrix molecular weight M_n was less than the graft molecular weight, but not when the matrix M_n was equal to or greater than the graft M_n. The threshold of electrical conductivity of the composites as a function of weight percent SWCNT increased from 0.2% when matrix M_n was less than graft M_n to about 1% when matrix M_n was greater than graft M_n. Dynamic mechanical analyses of the composites having graft M_n less than or equal to matrix M_n showed broader rubbery plateaus with increased SWCNT content but no significant differences between samples with different grafted PMMAs. The results indicate that lower M_n matrix wets the SWCNT‐g‐PMMA whereas higher M_n matrix does not wet the SWCNT‐g‐PMMA. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 39884.