Fabrication,characterization, and performance of YbDSB ternary compounds for IT‐SOFC applications |
| |
| Authors: | Serdar Yilmaz Esra Yildiz Bekir Kavici |
| |
| Affiliation: | 1. Department of Physics, Mersin University, Mersin, Turkey;2. Department of Chemistry, Bozok University, Yozgat, Turkey |
| |
| Abstract: | (Yb2O3)x(Dy2O3)y(Bi2O3)1?x?y (0.04≤x+y≤0.20) powders (xYbyDSB) were synthesized by modified sol‐gel Pecchini method. The powders were characterized for structural, surface morphological, thermal, and electrical properties and power density measurements by means of X‐ray diffraction (XRD), scanning electron microscopy (SEM), differential thermal analysis/thermal gravimetry (DTA/TG), and impedance spectroscopy, respectively. Lattice parameters and crystalline size of δ‐phase of Yb2O3‐ and Dy2O3‐doped Bi2O3 samples were calculated from the X‐ray diffraction data. Surface and grain properties of the related phases were determined by SEM analysis. In the investigated system, the maximum electrical conductivity was observed as σ=0.954 S cm?1 for 6% mol Yb2O3 and 6% mol Dy2O3 at 800°C among all δ‐YbDSB systems. Cathode supported electrochemical cell was fabricated and 6Yb6DSB was used as the electrolyte. Maximum power density of single cell with an active area of 1.5 cm2 is 72.50 mW/cm2 at 700°C. |
| |
| Keywords: | doped bismuth oxides Pechini method solid electrolytes solid oxide fuel cell tape casting |
|
|