Low temperature sintering of Si3N4 ceramics by spark plasma sintering technique

Abstract

Abstract

Low temperature sintering of α‐Si₃N₄ matrix ceramics was developed in the present study using 4?wt‐%MgO together with Al₂O₃ or AlPO₄ as the sintering additives and spark plasma sintering technique. The results suggested that α‐Si₃N₄ ceramics could be densified at low sintering temperature by adjusting both the sintering temperature and sintering additive content. For low temperature sintered α‐Si₃N₄ ceramics, using MgO and Al₂O₃ as the sintering additives, the densification is not complete at a temperature lower than 1600°C, and the mechanical strength is <200?MPa. When MgO and AlPO₄ were used as the sintering additives, the increase in AlPO₄ content not only declines the sintering temperature but also promotes the mechanical property of the sintered Si₃N₄ ceramics. It was the AlPO₄ phosphate binder that played a significant role in low temperature sintering of Si₃N₄ ceramics.