Synthesis of tetramethyl-p-silphenylenesiloxanedimethylsiloxane triblock copolymer by employing living anionic polymerization

Dimethylsiloxane-tetramethyl-p-silphenylenesiloxane-dimethylsiloxane (DMS-TMPS-DMS) triblock copolymer was synthesized by employing living anionic polymerization of hexamethylcyclotrisiloxane (D₃). Two synthetic methods were carried out for the polymerization. One of those methods was the anionic polymerization of D₃ initiated at the silanolate anion which was prepared from the terminal hydroxyl group of silanol-terminated TMPS prepolymer by reaction with n-butyllithium (method 1). The other was the coupling reaction of vinyl-terminated TMPS prepolymer with hydrosilyl-terminated DMS prepolymer obtained from the anionic polymerization of D₃ by using diphenylmethylsilanolate anion as initiator (method 2). In method 1, DMS contents of the copolymers ranged from 25.8 to 72.5 wt% and the values agreed with the ratio of D₃ to TMPS prepolymer. The weight-average molecular weights ranged from 1.36×10⁴ to 19.4×10⁴ and were close to the predicted values calculated from the $\text{M}\text{?}{}_{\mathrm{v}}$ of the TMPS prepolymer and the amount of D₃ added. In the case of method 2, weight-average molecular weights ranged from 19.5×10⁴ to 24.2×10⁴. The high molecular weight copolymer could thus be obtained by method 2. Intrinsic viscosity values of the triblock copolymers agreed with calculated values obtained by considering the copolymer as a binary mixture of these homopolymers. Differential scanning calorimetry and thermogravimetry were carried out on the triblock copolymers. The equilibrium melting temperatures of each of the copolymers were very close to that of poly-TMPS (160°C). The glass transition temperature and heat of fusion were decreased as the DMS content was increased. The thermogravimetric curves for the copolymers indicated that the thermal stability of the triblock copolymer was intermediate between the DMS and TMPS homopolymers.