Fabrication and upconversion luminescence properties of Er:SrF2 transparent ceramics compared with Er:CaF2

SrF₂ transparent ceramic is a promising upconversion material due to the low phonon energy. The effect of different sintering temperatures on Er:SrF₂ transparent ceramics was investigated. The suitable sintering temperature for Er:SrF₂ transparent ceramics was 900 °C by hot-pressed sintering in this study. High quality of Er:SrF₂ transparent ceramics with different doping concentrations were obtained. The upconversion luminescence spectra and decay behavior were compared between Er:SrF₂ and Er:CaF₂ transparent ceramics with different Er³⁺ doping concentration. The green emission of 5 at.% Er:SrF₂ ceramic was much stronger than that of 5 at.% Er:CaF₂ ceramic, while the red emission of Er:SrF₂ ceramic was almost the same as that of Er:CaF₂ ceramic. The upconversion luminescence lifetime of Er:SrF₂ transparent ceramics was longer than that of Er:CaF₂.All the results indicated Er:SrF₂ transparent ceramics was a candidate for green fluorescent upconversion materials.