Effect of substrate on the microstructure and thermoelectric performances of Sr-doped Ca3Co4O9 thick films

Ca₃Co₄O₉ thermoelectric materials in form of thick films are very promising in practical applications due to their low costs and relatively high performance. In this work, two different suspensions have been used to produce different coatings on Al₂O₃ polycrystalline substrates with theoretical green thickness of 360 and 2000?µm. Moreover, the effect of substrate has also been investigated using Al₂O₃ monocrystalline substrates and a 360?µm green thickness. Sintering procedure at 900?°C for 24?h has drastically decreased coating thickness. XRD performed on the coatings surface has shown the formation of small amounts of Ca₃Co₂O₆ secondary phase on the polycrystalline substrates, while it was more abundant, and accompanied by Ca₂Co₂O₅ on the monocrystalline substrates. In spite of the higher secondary phases content, monocrystalline substrates produced a slight grain orientation which led to the highest thermoelectric properties between the samples (0.38?mW/K²m at 800?°C), and very close to the best reported values in the literature.