Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

SiC composite ceramics have good mechanical properties. In this study, the effect of temperature on the microstructure and mechanical properties of SiC–TiB₂ composite ceramics by solid-phase spark plasma sintering (SPS) was investigated. SiC–TiB₂ composite ceramics were prepared by SPS method with graphite powder as sintering additive and kept at 1700 °C, 1750 °C, 1800 °C and 50 MPa for 10min.The experimental results show that the proper TiB₂ addition can obviously increase the mechanical properties of SiC–TiB₂ composite ceramics. Higher sintering temperature results in the aggregation and growth of second-phase TiB₂ grains, which decreases the mechanical properties of SiC–TiB₂ composite ceramics. Good mechanical properties were obtained at 1750 °C, with a density of 97.3%, Vickers hardness of 26.68 GPa, bending strength of 380 MPa and fracture toughness of 5.16 MPa m^1/2.