Enhanced near-infrared to green upconversion from Er3+-doped oxyfluoride glass and glass ceramics containing BaGdF5 nanocrystals

In this work, effect of glass composition as well as ceramization on visible and near-infrared (NIR) luminescence properties along with their decay dynamics of Er³⁺ ions has been compared considering two different oxyfluoride glasses yielding BaF₂ and BaGdF₅ nanocrystals. Both the glass systems have exhibited an intense normal and upconversion green emission under ultraviolet (378 nm) and NIR (978 nm) excitations, respectively. A remarkable enhancement of these emission intensities is observed for gadolinium-(Gd) containing glasses. Interestingly, NIR fluorescence intensity from Er³⁺ ions at 1540 nm has showed marginal decrease in gadolinium-containing glass which is attributed to occurrence of strong excited-state absorption (ESA) due to higher fluorine content ensuing an augmentation of upconversion green emission with a concomitant decrease in NIR emission. The quadratic dependence of upconversion green emission intensity on its pump power for all the samples revealed biphotonic absorption process from ground-state ⁴I_15/2 to the excited-state ⁴I_11/2 followed by ESA of second photon to the ⁴F_7/2 level. The intense green upconversion emission as well as enhanced NIR fluorescence lifetimes indicate the suitability of these glass/glass ceramics for upconversion lasers and amplification in the third telecom window.