| Photoluminescence properties of M2ZnSi2O7:Eu2+（M=Sr,Ba） |
| |
| 引用本文： | 姚山山,薛丽红,严有为.Photoluminescence properties of M2ZnSi2O7:Eu2+（M=Sr,Ba）[J].中国稀土学报(英文版),2010(Z1):265-268. |
| |
| 作者姓名： | 姚山山 薛丽红 严有为 |
| |
| 作者单位： | State Key Laboratory of Materials Processing and Die & Mould Technology,College of Materials Science and Engineering,Huazhong University of Science & Technology |
| |
| 基金项目： | Project supported by the National Natural Science Foundation of China (51002054);Natural Science Foundation of Hubei Province of China (2008CB252);SRF for ROCS,SEM,and the Special Funds of Central Colleges Basic Scientific Researh Operating Expenses |
| |
| 摘 要： | The hardystonite phosphors of Eu2+ activated M2ZnSi2O7(M=Sr,Ba) were synthesized by combustion-assisted method.They were systematically characterized by photoluminescence excitation and emission spectra.The emission spectra of these two phosphors showed that the main emission peaks are at 475 and 503 nm due to 4f65d1→4f7 transition of Eu2+.Both phosphors could be efficiently excited in the wavelength range of 250-425 nm where the near ultraviolet light-emitting diode was well matched.The(x,y) color coordinates were determined with the emission values(x,y)=(0.41,0.21) and(0.16,0.45) for the M2ZnSi2O7:Eu2+(M=Sr,Ba) phosphors.
|
| 关 键 词： | optical materials optical properties luminescence rare earths |
Photoluminescence properties of M<sub>2</sub>ZnSi<sub>2</sub>O<sub>7</sub>:Eu<sup>2+</sup>（M=Sr,Ba） |
| |
| YAO Shanshan,XUE Lihong,YAN Youwei.Photoluminescence properties of M2ZnSi2O7:Eu2+（M=Sr,Ba）[J].Journal of Rare Earths,2010(Z1):265-268. |
| |
| Authors: | YAO Shanshan XUE Lihong YAN Youwei |
| |
| Affiliation: | (State Key Laboratory of Materials Processing and Die & Mould Technology,College of Materials Science and Engineering,Huazhong University of Science & Technology,Wuhan 430074,China) |
| |
| Abstract: | The hardystonite phosphors of Eu2+ activated M2ZnSi2O7(M=Sr,Ba) were synthesized by combustion-assisted method.They were systematically characterized by photoluminescence excitation and emission spectra.The emission spectra of these two phosphors showed that the main emission peaks are at 475 and 503 nm due to 4f65d1→4f7 transition of Eu2+.Both phosphors could be efficiently excited in the wavelength range of 250-425 nm where the near ultraviolet light-emitting diode was well matched.The(x,y) color coordinates were determined with the emission values(x,y)=(0.41,0.21) and(0.16,0.45) for the M2ZnSi2O7:Eu2+(M=Sr,Ba) phosphors. |
| |
| Keywords: | optical materials optical properties luminescence rare earths |