Fe-Si-B非晶带材高温氧化行为及回收工艺

Oxidation behavior and recycling process of Fe- Si- B amorphous ribbon

??In order to reduce the oxidative burning loss of Fe78Si9B13 amorphous ribbon in the recovery process?? the oxidation behavior of Fe78Si9B13 amorphous ribbon was studied. The results show that the oxidation of Fe78Si9B13 amorphous ribbon at high temperature is related to the heating rate. The oxidation weight gain of Fe78Si9B13 amorphous ribbon at 5 and 10K/min from room temperature to 1223K are 44% and 31% respectively. There is an oxide layer with loose texture and a small amount of microcrack at the interface between the sample and atmosphere by SEM. The oxide layer contains a large amount of Fe2O3 and a little SiO2 by XRD. Oxidation kinetics curve shows that the oxidation weight gain of the samples follows a linear rule within 5hours at 1073 and 1173K?? then a parabolic rule. At 1273K?? however?? it only follows a linear rule?? meanwhile the oxidation speed is very fast?? with the oxidation weight gain reaches 40% in 12min. The oxidation weight gain in the amorphous ribbon recycling process can be reduced through cutting down the furnace gas temperature?? compressing the waste ribbon and unqualified products in the packaging process and blowing argon to reduce the partial pressure of oxygen in the furnace. Thus the slag decreases to 9-10g when 1kg waste ribbon is recovered?? and the Si content of liquid alloy increases to 8. 9%.