| AISI 410SS钢Φ200 mm锻材轴心晶间裂原因分析与工艺改进 |
| |
| 引用本文： | 张军,李造宇,杨玲,郑振宇,杨娥,伍伟.AISI 410SS钢Φ200 mm锻材轴心晶间裂原因分析与工艺改进[J].特殊钢,2020,41(5):52-54. |
| |
| 作者姓名： | 张军 李造宇 杨玲 郑振宇 杨娥 伍伟 |
| |
| 作者单位： | 1大冶特殊钢有限公田，黄G 435001 ；
2湖北省黄石市产品质量监督检捡所，黄石435000 ；
3高品质特殊钢湖北省币点实验室，黄石435001; |
| |
| 摘 要： | 规格Φ200 mm的AISI 410SS钢生产流程为20t电弧炉冶炼→LF→VD→3t铸锭→锻造。通过对轴心晶间裂的微观形貌、形成机理进行综合分析,钢液凝固过程中心部位置冷却慢导致成分偏析而形成的铁素体增加和夹杂物聚集,最终导致锻材轴心晶间裂。通过对成分进行调整,奥氏体形成元素分别由原0.11C-0.16Ni-0.55Mn增加至0.14C-0.45Ni-0.78Mn和铁素体形成元素由原12.84Cr-0.46Si-0.20Mo-0.0022 Nb减少至11.81Cr-0.31Si-0.10Mo-0.005Nb,铁素体由4%降至0.5%,轴心晶间裂由0.5级降至0级
|
| 关 键 词： | AISI410SS钢 轴心品间裂 铁素体 |
| 收稿时间： | 2020-04-05 |
Cause Analysis and Process Improvement of Centre Intergranular Crack of Φ200 mm Forging of Steel AISI 410SS |
| |
| Zhang Jun,Li Zaoyu,Yang Ling,Zheng Zhenyu,Yang E,Wu We.Cause Analysis and Process Improvement of Centre Intergranular Crack of Φ200 mm Forging of Steel AISI 410SS[J].Special Steel,2020,41(5):52-54. |
| |
| Authors: | Zhang Jun Li Zaoyu Yang Ling Zheng Zhenyu Yang E Wu We |
| |
| Affiliation: | 1 Daye Special Steel Co Ltd,Huangshi 435001 ；
2 Hubei Huangsh) Product Quality Supervision and Inspection Institute,Huangshi 435000;
3 Hubei province Key Laboratory for High Quality Special Steel； Huangshi 435001) |
| |
| Abstract: | The production process of Φ200 mm steel AISI 410SS is 20 t EAF-LF-VD-3 t ingot-forging. Through comprehensive analysis on the micro-morphology and formation mechanism of centre intergranular cracks, it is found that slow cooling of the central part of the liquid steel during solidification results in composition segregation, increasing ferrite formation and inclusion clustering finally led to forgings axis intergranular cracks. By adjusting the composition, increasing austenite-forming elements from original 0.11C-0.16Ni~0.55Mn to 0.14C-0.45Ni-0.78Mn and reducing ferrite-forming elements from original 12.84Cr-0.46S1-0.20Mo-0.022Nl)to 11.81Cr-0.31 Si-0.l0Mo-O.005Nb, the ferrite in steel decreases from original 4% to 0. 5% and the axis intergranular crack rating decreases for 0.5 rating to 0. |
| |
| Keywords: | Steel AISI 410SS Axial Intergranular Crack Ferrite |
| 本文献已被 CNKI 等数据库收录！ |
| 点击此处可从《特殊钢》浏览原始摘要信息 |
|
点击此处可从《特殊钢》下载全文 |
|