Fabrication of Ultrafine-Grained Gradient Cemented Carbide by SPS Pre-sintered Method |
| |
| XU Zhi-feng,ZHOU Xiang-kui,WANG Kai,WANG Qiang.Fabrication of Ultrafine-Grained Gradient Cemented Carbide by SPS Pre-sintered Method[J].Journal of Northeastern University(Natural Science),2018,39(11):1593-1597. |
| |
| Authors: | XU Zhi-feng ZHOU Xiang-kui WANG Kai WANG Qiang |
| |
| Affiliation: | 1. Key Laboratory of Electromagnetic Processing of Materials， Ministry of Education， Northeastern University， Shenyang 110819， China; 2. Mechanical and Electrical Engineering Institute， Zhengzhou University of Light Industry， Zhengzhou 450002， China. |
| |
| Abstract: | The ultrafine-grained gradient cemented carbide (UGCC) was prepared by a two-step sintering， containing spark plasma or vacuum pre-sintering， and a gradient sintering. The effect of the pre-sintering mode (spark plasma or vacuum)on microstructure of the UGCC is studied and the influence of the pre-sintered microstructure on the gradient formation and grain growth during gradient sintering process is also analyzed. The results show that the pre-sintered microstructure of the UGCC greatly affects the gradient formation and grain growth during gradient sintering. Using this two-step sintering， the thickness of gradient layer of the UGCC can be increased to 53μm， associated with the average grain size of WC about 0.3μm. |
| |
| Keywords: | ultrafine grain gradient cemented carbide SPS(spark plasma sintering) pre-sintering gradient formation grain size |
|