High-frequency induction heated sintering of ball milled Fe-WC nanocomposites |
| |
Authors: | M Zakeri T Zanganeh A Najafi |
| |
Affiliation: | 1785. Ceramic Department, Materials and Energy Research Center, P.O. Box 31787/316, Karaj, Iran 2785. Department of Materials, Saveh Branch, Islamic Azad University, Saveh, Iran
|
| |
Abstract: | Fe-WC nanocomposites were successfully fabricated by high-frequency induction heated sintering of ball milled nanostructure powders. The ball milled powders were characterized by X-ray diffraction. Density measurements by the Archimedes method show that all sintered samples have the relative density higher than 95%. Studies on the effects of WC content, milling speed, and milling time indicate that a higher milling speed and a more WC content lead to the improvement of mechanical properties. There is a very good distribution of WC particles in the Fe matrix at the milling speed of 650 r/min. For the sintered sample 20-5-650 (20wt% WC, milling time of 5 h, and milled speed of 650 r/min), the maximum Brinell hardness and yield stress are obtained to be 3.25 GPa and 858 MPa, respectively. All sintered samples have brittle fracture during compression test except the sample 20-5-650. |
| |
Keywords: | |
本文献已被 万方数据 SpringerLink 等数据库收录! |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
|
点击此处可从《矿物冶金与材料学报》下载全文 |
|