| Abstract: | This paper investigates three aspects of linear-low-density polyethylene (LLDPE) rheological properties: shear viscosity variations with shear rate and temperature, tensile behavior determined with an extensiometer, and extrusion defects. The differences in shear viscosity variation with shear rate and temperature between LLDPE and LDPE (low-density polyethylene) are shown. These differences, attributed to wider molecular weight distribution and to long chain branching (LCB) in LDPE, involve different extrusion behaviors. The lack of LCB in LLDPE can be demonstrated by comparison of the measured Newtonian viscosity with the value of the same parameter calculated from molecular weight distribution and composition law of Newtonian viscosities. The lack of LCB leads to good melt extensibility, which is shown by tensile properties of polyethylene melts determined with a non-isothermal extensiometer. The melt fracture phenomenon is studied because it promotes surface defects on bubbles in film application. Extrudate distortions are examined at the laboratory extruder outlet. This test shows differences between LLDPE and LDPE, but also between some LLDPE samples. |