Influence of K2TiF6 additive on the hydrogen sorption properties of MgH2

In this study, the hydrogen storage properties of MgH₂ with the addition of K₂TiF₆ were investigated for the first time. The temperature-programmed desorption results showed that the addition of 10 wt% K₂TiF₆ to the MgH₂ exhibited a lower onset desorption temperature of 245 °C, which was a decrease of about 105 °C and 205 °C compared with the as-milled and as-received MgH₂, respectively. The dehydrogenation and rehydrogenation kinetics of 10 wt% K₂TiF₆-doped MgH₂ were also significantly improved compared to the un-doped MgH₂. The results of the Arrhenius plot showed that the activation energy for the hydrogen desorption of MgH₂ was reduced from 164 kJ/mol to 132 kJ/mol after the addition of 10 wt% K₂TiF₆. Meanwhile, the X-ray diffraction analysis showed the formation of a new phase of potassium hydride and titanium hydride together with magnesium fluoride and titanium in the doped MgH₂ after the dehydrogenation and rehydrogenation process. It is reasonable to conclude that the K₂TiF₆ additive doped with MgH₂ played a catalytic role through the formation of active species of KH, TiH₂, MgF₂ and Ti during the ball milling or heating process. It is therefore proposed that this newly developed product works as a real catalyst for improving the hydrogen sorption properties of MgH₂.