Texture,microstructures, and mechanical properties of AlN‐based ceramics with Si3N4–Y2O3 additives

Textured AlN‐based ceramics with improved mechanical properties were prepared by hot pressing using Si₃N₄ and Y₂O₃ as additives. The introduction of Si₃N₄–Y₂O₃ into AlN matrix led to the formation of secondary Y₃AlSi₂O₇N₂ and fiber‐like 2H^δ AlN‐polytypoid phases, the partial texture of all crystalline phases, and the fracture mode change from intergranular to transgranular. Consequently, Vickers hardness, fracture toughness and flexural strength of AlN‐based ceramics by the replacement of Y₂O₃ by Si₃N₄–Y₂O₃ increased significantly from 10.4±0.3 GPa, 2.4±0.3 MPa m^½ and 333.3±10.3 MPa to 14.2±0.4 GPa, 3.4±0.1 MPa m^½ and 389.5±45.5 MPa, respectively.