| 摘 要： | 将La0.67Sr0.33MnO3（LSMO）、Ag2O及TiO2粉混合经高温烧结后制备了钙钛矿相/xAg两相复合体系（x是Ag与钙钛矿材料的物质的量比）,系统地研究了Ag-Ti的共掺杂对LSMO电性和磁电阻效应的影响.0.07摩尔比Ti4＋离子的B位掺杂使LSMO的居里温度降至室温.Ag的掺入对Tc影响不大,Tp逐渐升高.由于钙钛矿颗粒属性的改善和金属导电通道的出现,材料的电阻率明显下降.Ag掺杂使室温磁电阻得到显著增强,室温下从x=0.30样品中得到最大的磁电阻,约为32%,是La0.67Sr0.33MnO3样品的8倍,La0.67Sr0.33Mn0.93Ti0.07O3样品的1.6倍.
|
| 关 键 词： | 钙钛矿锰氧化物 Ag掺杂的锰氧化物 两相复合体系 室温磁电阻 |
| 文章编号： | 1007-4252(2007)02-0181-04 |
| 修稿时间： | 2006年3月24日 |
Doping effect of Ag-Ti in La0.67 Sr0.33 MnO3 |
| |
| WANG Jun-hua,HUANG Bao-xin,YUAN Xiao-bo,WANG Cheng-jian,LIU Yi-hua,MEI Liang-mo.Doping effect of Ag-Ti in La0.67 Sr0.33 MnO3[J].Journal of Functional Materials and Devices,2007,13(2):181-184. |
| |
| Authors: | WANG Jun-hua HUANG Bao-xin YUAN Xiao-bo WANG Cheng-jian LIU Yi-hua MEI Liang-mo |
| |
| Abstract: | The composite of perovskite /xAg(x is the nominal molar ratio of Ag)was prepared by calcining the mixture of La0.67Sr0.33MnO3(LSMO),TiO2 and Ag2O powders.The effects of Ag-Ti addition in LSMO on the electric and magnetoresistance properties were studied systematically.The Curie temperature of LSMO lowers successfully to room temperature with 0.07 mol ratio Ti4+ addition.With increasing Ag content,TC of the samples changes slightly while TP increases gradually.The resistivity decreases remarkably due to better crystallization of the pervoskite grains and metal conduction channels provided by Ag addition.The magnetoresistance at room temperature is remarkably enhanced by Ag addition.A maximum MR ratio of 32 % at room temperature is obtained for the samples with x = 0.30,which is approximately 8 times and 1.6 times as large as that for La0.67Sr0.33MnO3 and La0.67Sr0.33Mn0.93Ti0.07O3,respectively. |
| |
| Keywords: | perovskite manganites Ag-added manganites two-phase composites room temperature magnetoresistance |