Synthesis of a novel langanite-type compound La3Al5.5Nb0.5O14 by the sol-gel process

Langanite (La₃Ga_5.5Nb_0.5O₁₄, LGN) and its isomorphs are a few piezoelectric materials which have the unique temperature compensation and piezoelectric properties. But the high Ga₂O₃ content makes them very expensive and limits their applications. We reported a new langanite-type compound La₃Al_5.5Nb_0.5O₁₄ (LAN) which has the advantage of no Ga₂O₃ content. Chemically homogeneous La₃Al_5.5Nb_0.5O₁₄ sol was synthesized using La (NO₃)₃·6H₂O, Al (NO₃)₃·9H₂O and niobium citrate as starting materials. Single-phased LAN powder was prepared by decomposition of a citrate polymer precursor and subsequent reactions at high temperatures. TG-DTA, XRD and FTIR were employed to investigate the transformation process of gel to LAN powder. The results showed that, after calcination at 900 °C, pure La₃Al_5.5Nb_0.5O₁₄ polycrystalline powder with a narrow particle size distribution was obtained, which has the same structure with La₃Ga_5.5Nb_0.5O₁₄.