苯并三唑对碳钢/铜合金电偶腐蚀行为的影响
引用本文:王琳,周漪,李传鹏,刘杰.苯并三唑对碳钢/铜合金电偶腐蚀行为的影响[J].表面技术,2022,51(2):259-267.
作者姓名:王琳  周漪  李传鹏  刘杰
作者单位:海军航空大学 航空基础学院,山东 烟台 264001;西南技术工程研究所 国防科技工业自然环境试验研究中心,重庆 400039;烟台大学 化学化工学院,山东 烟台 264005
基金项目:国家自然科学基金(51971192,51901096);烟台市科技计划(2019XDHZ086)
摘    要:目的 研究NaCl溶液中苯并三唑(BTA)对碳钢/铜合金电偶腐蚀行为的影响.方法 使用丝束电极(WBE)技术和电化学阻抗谱(EIS)技术研究在未添加和添加BTA的NaCl溶液中,丝束电极表面的电位分布、电流密度分布和电化学阻抗谱演化,同时对比分析碳钢区域与铜合金区域的阻抗谱特征.结果 在未添加BTA的条件下浸泡72 h...

关 键 词:电偶腐蚀  碳钢  铜合金  缓蚀作用  丝束电极  电化学阻抗谱
收稿时间:2020/8/21 0:00:00
修稿时间:2021/8/9 0:00:00

Effect of 1H-benzotriazole on Galvanic Corrosion Behavior of Carbon Steel/Copper Alloy
WANG Lin,ZHOU Yi,LI Chuan-peng,LIU Jie.Effect of 1H-benzotriazole on Galvanic Corrosion Behavior of Carbon Steel/Copper Alloy[J].Surface Technology,2022,51(2):259-267.
Authors:WANG Lin  ZHOU Yi  LI Chuan-peng  LIU Jie
Affiliation:Aviation Foundation College, Naval Aviation University, Yantai 264001, China;Weathering Test and Research Center of Science Technology and Industry for National Defense, Southwest Technology and Engineering Research Institute, Chongqing 400039, China;School of Chemistry and Chemical Engineering, Yantai University, Yantai 264005, China
Abstract:The work aims to study the effect of 1H-benzotriazole (BTA) in NaCl solution on the galvanic corrosion behavior of carbon steel/copper alloy. The potential distribution, current density distribution and EIS evolution of the WBE in NaCl solution with and without BTA were studied by the wire beam electrode (WBE) and electrochemical impedance spectroscopy (EIS) techniques. Meanwhile, the EIS characteristics of the carbon steel area and the copper alloy area were compared and analyzed. After immersion for 72 h under the condition without BTA, the anodic current area on the carbon steel surface accounted for 80%, and the range of current density distribution was narrow. After immersion for 72 h under the condition with BTA, the proportion of anode area on the surface of carbon steel was 86%, and the range of current density distribution was significantly enlarged. The impedance value of the copper alloy under the condition with corrosion inhibitor was greater than that of the copper alloy under the condition without corrosion inhibitor. However, the impedance value of carbon steel in the solution with and without BTA was relatively small. When copper alloy and carbon steel are electrically coupled in NaCl solution, the electrochemical inhomogeneity of carbon steel is increased due to corrosion inhibition effect of BTA. In the galvanic corrosion process of carbon steel/copper alloy, BTA only plays a good corrosion inhibition effect on the copper alloy, and the corrosion inhibition effect of BTA on carbon steel is not obvious. Compared with the carbon steel/copper alloy couple, when the copper alloy is individually immersed in a solution containing BTA, the Cu-BTA molecular film formed on the surface is more stable and the corrosion inhibition effect is better. With the extension of the immersion time, the electrode reaction rates of the WBE in the NaCl solution added with BTA are gradually increased, while the changes of the electrode reaction rates of the WBE under the conditions without BTA are exactly the opposite.
Keywords:galvanic corrosion  carbon steel  copper alloy  corrosion inhibition  WBE  EIS