| Influence of heat treatment on nanocrystalline zirconia powder and plasma-sprayed thermal barrier coatings |
| |
| 作者姓名： | 蒋显亮 ;刘纯波 ;刘敏 ;朱晖朝 |
| |
| 作者单位： | School of Materials Science and Engineering,Central South University Guangzhou Research Institute of Non-ferrous Metals |
| |
| 基金项目： | Project（1343-77212）supported by the Innovation Program for Graduate Students of Central South University,China |
| |
| 摘 要： | Nanostructured zirconia top coat was deposited by air plasma spray and NiCoCrAlTaY bond coat was deposited on Ni substrate by low pressure plasma spray.Nanostructured and conventional thermal barrier coatings were heat-treated at temperature varying from 1050 to 1 250oC for 2-20 h.The results show that obvious grain growth was found in both nanostructured and conventional thermal barrier coatings(TBCs)after high temperature heat treatment.Monoclinic/tetragonal phases were transformed into cubic phase in the agglomerated nano-powder after calcination.The cubic phase content increased with increasing calcination temperature.Calcination of the powder made the yttria distributed on the surface of the nanocrystalline particles dissolve in zirconia when grains grew.Different from the phase constituent of the as-sprayed conventional TBC which consisted of diffusionlesstransformed tetragonal,the as-sprayed nanostructured TBC consisted of cubic phase.
|
| 关 键 词： | nanocrystalline material zirconia thermal barrier coating heat treatment phase composition |
| 收稿时间： | 23 November 2009 |
Influence of heat treatment on nanocrystalline zirconia powder and plasma-sprayed thermal barrier coatings |
| |
| JIANG Xian-liang,LIU Chun-bo,LIU Min,ZHU Hui-zhao.Influence of heat treatment on nanocrystalline zirconia powder and plasma-sprayed thermal barrier coatings[J].Transactions of Nonferrous Metals Society of China,2010,20(12):2272-2280. |
| |
| Authors: | JIANG Xian-liang LIU Chun-bo LIU Min ZHU Hui-zhao |
| |
| Affiliation: | [1]School of Materials Science and Engineering, Central South University, Changsha 410083, China; [2]Guangzhou Research Institute of Non-ferrous Metals, Guangzhou 510651, China |
| |
| Abstract: | Nanostructured zirconia top coat was deposited by air plasma spray and NiCoCrAlTaY bond coat was deposited on Ni substrate by low pressure plasma spray. Nanostructured and conventional thermal barrier coatings were heat-treated at temperature varying from 1050 to 1 250 °C for 2-20 h. The results show that obvious grain growth was found in both nanostructured and conventional thermal barrier coatings (TBCs) after high temperature heat treatment. Monoclinic/tetragonal phases were transformed into cubic phase in the agglomerated nano-powder after calcination. The cubic phase content increased with increasing calcination temperature. Calcination of the powder made the yttria distributed on the surface of the nanocrystalline particles dissolve in zirconia when grains grew. Different from the phase constituent of the as-sprayed conventional TBC which consisted of diffusionless-transformed tetragonal, the as-sprayed nanostructured TBC consisted of cubic phase. |
| |
| Keywords: | nanocrystalline material zirconia thermal barrier coating heat treatment phase composition |