| 摘 要： | 采用Ag-28Cu银基钎料对钛/钢进行真空钎焊。研究钛/钢钎焊接头的拉剪强度、界面微观组织演变与断裂行为的特征，确定不同钎焊工艺对接头拉剪强度和成分分布的影响。结果表明，钛/钢结合界面形成不同的金属间化合物，如CuTi、CuTi2、Cu4Ti3、FeTi等，并且接头微观组织对钎焊试样的拉剪强度有显著影响。接头最高拉剪强度可达100 MPa。不同钎焊条件下断口形貌发生变化，但断裂都是发生在钛/银基合金界面上。
|
| 关 键 词： | 银基钎料 真空钎焊 钛 钢 |
| 收稿时间： | 2017/8/15 0:00:00 |
Microstructure and Properties of Vacuum Brazed Titanium/Steel Joints Using Silver-based Filler Metal |
| |
| YUAN Linlin,LI Bin,WANG Ran,QI Yu,JIAO Lei and QI Yuefeng.Microstructure and Properties of Vacuum Brazed Titanium/Steel Joints Using Silver-based Filler Metal[J].Precious Metals,2017,38(S1):01-6. |
| |
| Authors: | YUAN Linlin LI Bin WANG Ran QI Yu JIAO Lei and QI Yuefeng |
| |
| Affiliation: | Beijing Non-ferrous Metals and Rare Earth Research Institute, Beijing 100012, China;Beijing Engineering Research Center of New Brazing Materials for Electronic Information, Beijing 100012, China,Beijing Non-ferrous Metals and Rare Earth Research Institute, Beijing 100012, China,Beijing Non-ferrous Metals and Rare Earth Research Institute, Beijing 100012, China,Beijing Non-ferrous Metals and Rare Earth Research Institute, Beijing 100012, China,Beijing Non-ferrous Metals and Rare Earth Research Institute, Beijing 100012, China and Beijing Engineering Research Center of New Brazing Materials for Electronic Information, Beijing 100012, China |
| |
| Abstract: | The Ag-28Cu silver-based filler metal was used to vacuum braze titanium/steel joints. The tensile-shear strength, microstructure and the fracture morphology of brazed joints were investigated and the effects of the different process parameters on the tensile-shear strength and the component distribution were identified. The results show that the different intermetallic compounds such as CuTi, CuTi2, Cu4Ti3 and FeTi were formed in the titanium/steel interface. It was observed that the microstructures of joints have considerable effect on the tensile-shear strength of the brazed samples. The peak value of the tensile-shear strength reached to 100 MPa. All of the fracture paths after the tensile-shear tests occurred in the interface between titanium and silver-based interlayer in spite of different the fracture morphologies. |
| |