Molecular beam epitaxial growth of SmBa2Cu3O7−δ thin films and effect of substrate temperature on the surface roughness

Stoichiometrically optimized, epitaxial SmBa₂Cu₃O_7-δ thin films with high T_{c, R = 0} and high critical current densities j_c have been prepared for the first time in a tightly controlled molecular beam epitaxy process in non-reactive molecular oxygen, followed by an in situ loading process with molecular oxygen. The surface roughness (on a submicrometre scale) of single-crystal films with their c axes perpendicular to the surface depends markedly on the surface temperature of the substrate during the deposition of the epitaxial films, within a range of only a few degrees centigrade. The calibrated optimal temperature for the preparation of epitaxial films 200 nm thick of this single orientation is found to be 680 ± 5 °C. In scanning tunnelling microscopy investigations, they show a surface roughness of less than 6 nm (five SmBa₂Cu₃O_7?δ unit cells) on a 2 μm × 2 μm scale. At deposition temperatures below this optimal deposition temperature, the well-known a-axis growth increases rapidly, whereas higher temperatures give a significantly higher surface roughness, which can be observed by scanning electron microscopy.