| Abstract: | High-energy ball milling (HEBM) combined with powder metallurgy route was used to fabricate carbon nanotube (CNT) reinforced 7055Al composites.Two powder morphology evolution processes (HEBM-1 and HEBM-2) were designed to investigate the dispersion and damage of CNTs during HEBM process.HEBM-1 evolution process involved powder flattening,cold-welding and fracture,while HEBM-2 evolution process consisted of powder flattening and fracture.For HEBM-1,the repetitive fracture and cold-welding process was effective for dispersing CNTs.However,the powder flattening process in HEBM-2 was unsuccessful in dispersing CNTs due to two reasons: (1) the thickness of flaky Al powders exceeded the critical value,and (2) the clustered CNTs embedded in flaky Al powders could not be unravelled.Because of the broadening of D band and the appearance of a new defect-related D'band,product of ID/IG and full width half maximum of D band,rather than ID/IG,was used to evaluate the actual damage of CNTs.It indicates that the damage of CNTs was severe in powder flattening and fracture stages,while the damage of CNTs was small in powder cold-welding stage. |