可用于Ⅲ族氮化物生长的50mm 3C-SiC/Si(111)衬底的制备

利用新研制出的垂直式低压CVD(LPCVD)SiC生长系统,获得了高质量的50mm 3C-SiC/Si(111)衬底材料.系统研究了3C-SiC的n型和p型原位掺杂技术,获得了生长速率和表面形貌对反应气体中SiH4流量和C/Si原子比率的依赖关系.利用Hall测试技术、非接触式方块电阻测试方法和SIMS,分别研究了3C-SiC的电学特性、均匀性和故意调制掺杂的N浓度纵向分布.利用MBE方法,在原生长的50mm 3C-SiC/Si(111)衬底上进行了GaN的外延生长,并研究了GaN材料的表面、结构和光学特性.结果表明3C-SiC是一种适合于高质量无裂纹GaN外延生长的衬底或缓冲材料.

Preparation of 50mm 3C-SiC/Si(111) as Substrates Suited for Ⅲ-Nitrides

50mm SiC films with high electrical uniformity are grown on Si(111) by a newly developed vertical low-pressure chemical vapor deposition (LPCVD) reactor.Both in-situ n- and p-type doping of 3C-SiC are achieved by intentional introduction of ammonia and boron into the precursor gases.The dependence of growth rate and surface morphology on the C/Si ratio and optimized growth conditions is obtained.The best electrical uniformity of 50mm 3C-SiC films obtained by non-contact sheet resistance measurement is ±2.58%.GaN films are grown atop the as-grown 3C-SiC/Si(111) layers using molecular beam epitaxy (MBE).The data of both X-ray diffraction and low temperature photoluminescence of GaN/3C-SiC/Si(111) show that 3C-SiC is an appropriate substrate or buffer layer for the growth of Ⅲ-nitrides on Si substrates with no cracks.