Efficient and Stable Perovskite Solar Cells via Dual Functionalization of Dopamine Semiquinone Radical with Improved Trap Passivation Capabilities

Highly efficient planar heterojunction perovskite solar cells (PVSCs) with dopamine (DA) semiquinone radical modified poly(3,4‐ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) (DA‐PEDOT:PSS) as a hole transporting layer (HTL) were fabricated. A combination of characterization techniques were employed to investigate the effects of DA doping on the electron donating capability of DA‐PEDOT:PSS, perovskite film quality and charge recombination kinetics in the solar cells. Our study shows that DA doping endows the DA‐PEDOT:PSS‐modified PVSCs with a higher radical content and greater perovskite to HTL charge extraction capability. In addition, the DA doping also improves work function of the HTL, increases perovskite film crystallinity, and the amino and hydroxyl groups in DA can interact with the undercoordinated Pb atoms on the perovskite crystal, reducing charge‐recombination rate and increasing charge‐extraction efficiency. Therefore, the DA‐PEDOT:PSS‐modified solar cells outperform those based on PEDOT:PSS, increasing open‐circuit voltage (V _oc) and power conversion efficiency (PCE) to 1.08 V and 18.5%, respectively. Even more importantly, the efficiency of the unencapsulated DA‐PEDOT:PSS‐based PVSCs are well retained with only 20% PCE loss after exposure to air for 250 hours. These in‐depth insights into structure and performance provide clear and novel guidelines for the design of effective HTLs to facilitate the practical application of inverted planar heterojunction PVSCs.