Conversion of potassium titanate nanowires into titanium oxynitride nanotubes |
| |
Authors: | Wei Yen-Ju Peng Chih-Wei Cheng Ta-Ming Lin Huang-Kai Chen Yu-Liang Lee Chi-Young Chiu Hsin-Tien |
| |
Affiliation: | Department of Applied Chemistry, National Chiao Tung University, Hsinchu, Taiwan 30050, ROC. |
| |
Abstract: | Tunnel-structured potassium titanate with a K(3)Ti(8)O(17) phase was synthesized by direct oxidation of titanium powder mixed with KF(aq) in water vapor at 923 K. The reaction conditions were adjusted so that uniform single crystalline potassium titanate nanowires with 010] growth direction (length: 5-30 μm, diameter: 80-100 nm) were obtained. Nitridation of the nanowires by NH(3)(g) at 973-1073 K converted the titanate nanowires into rock-salt structured cubic phase single crystalline titanium oxynitride TiN(x)O(y) nanotubes (x = 0.88, y = 0.12, length = 1-10 μm, diameter = 150-250 nm, wall thickness = 30 - 50 nm) and nanorods (x = 0.5, y = 0.5, length = 1-5 μm, diameter = 100-200 nm) with rough surfaces and 200] growth direction. The overall conversion of the titanate nanowires into the nanotubes and the nanorods can be rationalized by Ostwald ripening mechanism. We fabricated an electrode by adhering TiN(x)O(y) nanotubes (0.2 mg) on a screen-printed carbon electrode (geometric area: 0.2 cm(2)). Electrochemical impedance spectroscopy demonstrated its charge transfer resistance to be 20Ω. The electrochemical surface area of the nanotubes on the electrode was characterized by cyclic voltammetry to be 0.32 cm(2). This property suggests that the TiN(x)O(y) nanostructures can be employed as potential electrode materials for electrochemical applications. |
| |
Keywords: | |
本文献已被 PubMed 等数据库收录! |
|