High strength and good ductility of casting Al-Cu alloy modified by PrxOy and LaxOy

A modified Al-Cu alloy with high tensile strength and ductility of about 574.0 MPa and 10.4%, respectively, was obtained by adding multiple rare earth oxides (Pr_xO_y and La_xO_y) as modifier. Compared with the unmodified Al-Cu alloy, the tensile strength and ductility of the modified sample were increased by 24.3% and 42.5%, respectively. The improvement both in the strength and ductility may attribute to the finer crystal grains and dendrites, more homogeneously distributed θ′ phase precipitates and the intermetallic compounds formed at the crystal grain boundaries as well as in the space of the dendrites.