Effect of Al2O3 on the electrical properties of ZnO-Pr6O11-based varistor ceramics

The effect of Al₂O₃ on the electrical properties of ZnO-Pr₆O₁₁-based ceramics is investigated in this work. The average grain size of ZnO increased as the Al₂O₃ content increased from 10.3 to 13.5 μm. It was found that a sample doped with Al₂O₃ of 0.005 mol% showed the highest nonlinear current-voltage characteristics with a nonlinear exponent of 43.8 and a leakage current of 0.66 μA. When the Al₂O₃ content was increased, the donor concentration was increased from 0.51×10¹⁸/cm³ to 1.59×10¹⁸/cm³, but the barrier height was decreased from 1.01 to 0.87 eV. The best electrical stability against aging stress was obtained by doping Al₂O₃ of 0.001 mol%.