Synthesis and microstructure of Ti2AlN ceramic by thermal explosion |
| |
| Affiliation: | 1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;2. Beijing Key Laboratory of Green Recovery and Extraction of Rare and Precious Metals, University of Science and Technology Beijing, Beijing 100083, China;3. State Key Laboratory of Iron and Steel Industry Environmental Protection, Beijing 100088, China;4. Energy Conservation and Environment Protection Co., Ltd, MCC Group, Beijing 100088, China;5. Central Research Institute of Building and Construction Co., Ltd, MCC Group, Beijing 100088, China |
| |
| Abstract: | Ti2AlN ceramic with a small amount of TiN was rapidly synthesized by the thermal explosion (TE) technique using Ti, Al and TiN as starting materials. The effects of the starting composition, the particle size of TiN and the compacts’ height on the phase composition and microstructure of obtained Ti2AlN ceramic were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results showed that high purity Ti2AlN ceramic containing 4% TiN could be fabricated at 700 °C for 2 min with a molar ratio of 1.1:1.1:1(Ti: Al: TiN). It was further found that small particle size of TiN and compacts’ height of 2–8 mm were beneficial to obtain high purity Ti2AlN. Finally, the formation mechanism of Ti2AlN ceramic via thermal explosion was proposed. |
| |
| Keywords: | Thermal explosion Microstructure |
| 本文献已被 ScienceDirect 等数据库收录！ |
|