Interface structure and mechanical property of the brazed joint of graphite and copper |
| |
Authors: | XIE Fengchun ZHANG Lixia FENG Jicai HE Peng |
| |
Affiliation: | State Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin, 150001 |
| |
Abstract: | A kind of self-made AgCuTiSn braze alloy powder was used to join graphite and copper. The whole brazing process was performed under vacuum circumstances at different temperatures (1033-1193 K) for several holding time (300-1800 s). According to scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and electron probe X-ray microanalysis (EPMA) results, the reaction products of the interface are TiC, Ti3Sn, Cu(s. s), Ag(s. s) and Cu-Sn compound. As the brazing parameters increase, the quantity of Ag(s. s) in the braze alloy and C fibers on graphite/AgCuTiSn interface reduce, while that of Cu (s. s) in the braze alloy improves. When the brazing temperature is 1093 K and holding time is 900 s, the joint can obtain the maximum room temperature shear strength 24 MPa. |
| |
Keywords: | graphite joining interfaces microstructure strength |
本文献已被 维普 万方数据 等数据库收录! |
|